Dependence of vacancy concentration on morphology of helium bubbles in oxide ceramics

Since the formation of helium bubbles degrades swelling property and thermal conductivity of minor actinide-containing mixed oxide (MA-MOX) fuel, it is essential to understand the conditions of the bubble formation. In order to examine the dependence of vacancy concentration on morphology of helium bubbles, helium was infused into (Zr,Fe)O2−x. The oxygen vacancy concentration was controlled by addition of solute Fe3+ into ZrO2. Helium was infused by hot isostatic pressing. The helium-infused specimens were observed by field emission scanning electron microscopy (FE-SEM) and field emission transmission electron microscopy (FE-TEM). In addition, X-ray fluorescence, X-ray diffraction analysis, conversion electron yield–X-ray absorption near-edge structure and FE-SEM/EDX (energy dispersive X-ray) analyses were also made to interpret the results of microstructure observations. As a result of the helium infusion treatment, numerous 0.5–10 nm bubbles were observed and its number density clearly depended on oxygen vacancy concentration. On the other hand, sizes of the helium nano-bubbles in all specimens were almost constant.

An investigation of kinetic reaction and decomposition of sodium uranate

For the management of severe accidents of sodium-cooled fast breeder reactor, the coolability of the fuel debris bed on a core support plate is a key concern during the post-accident heat removal phase. In an air ingress scenario, the reactions between the fuel and highly oxidized sodium are likely to form sodium uranoplutonate. This would negatively influence the coolability of the fuel debris bed due to a lowering of the thermal conductivity and density. This study has focused on the formation kinetics of sodium uranate from UO2 and liquid sodium including oxygen at a high concentration. In this paper, the experiments on reaction initiation temperatures, reaction rates, and the decomposition of sodium uranate are reported.