Susceptor coating materials applicable for SiC reactor cleaning

In order to develop a cleaning process for the silicon carbide chemical vapor deposition reactor, the susceptor coating materials are developed for protecting the susceptor from the etching by chlorine trifluoride gas. The chlorine trifluoride gas does not give a serious damage to the pyrolitic carbon film at the temperatures lower than 480 °C, at which temperature the quick and practical reactor cleaning process is expected to be possible

Quick and Practical Cleaning Process for Silicon Carbide Epitaxial Reactor

In order to develop a quick and practical cleaning process for the silicon carbide chemical vapor deposition reactor, the pyrolytic carbon-coated susceptor was used. The 30-μm-thick silicon carbide film was formed on the susceptor; the film was cleaning by chlorine trifluoride gas at 460 °C for 15 min. The remained fluorine was removed by the annealing at 900 °C in ambient hydrogen. The pyrolytic carbon surface did not suffer from any damage, because the pyrolytic carbon film surface morphology after the cleaning process was the same as that before the silicon carbide film deposition.