Kye-Hong Cho

Identification of Calcium Sulphoaluminate Formation between Alunite and Limestone.

This study was carried out to identify the conditions of formation of calcium sulphoaluminate (3CaO·3Al2O3·CaSO4) by the sintering of a limestone (CaCO3) and alunite [K2SO4·Al2(SO4)3·4Al(OH)3] mixture with the following reagents: K2SO4, CaCO3, Al(OH)3, CaSO4·2H2O, and SiO2. When K2SO4, CaCO3, Al(OH)3, CaSO4·2H2O were mixed in molar ratios of 1:3:6:3 and sintered at 1,200∼1,300 °C, only 3CaO·3Al2O3·CaSO4 and calcium langbeinite (2CaSO4·K2SO4) were generated. With an amount of CaO that is less than the stoichiometric molar ratio, 3CaO·3Al2O3·CaSO4 was formed and anhydrite (CaSO4) did not react and remained behind. With the amount of CaSO4 that is less than the stoichiometric molar ratio, the amounts of 3CaO·3Al2O3·CaSO4 and 2CaSO4·K2SO4 decreased, and that of CaO·Al2O3 increased. In the K2SO4-CaO-Al2O3-CaSO4-SiO2 system, to stabilize the formation of 3CaO·3Al2O3·CaSO4, 2CaSO4·K2SO4, and β-2CaO·SiO2, the molar ratios of CaO: Al2O3: CaSO4 must be kept at 3:3:1 and that of CaO/SiO2, over 2.0; otherwise, the generated amount of 3CaO·3Al2O3·CaSO4 decreased and that of gehlenite (2CaO·Al2O3·SiO2) with no hydration increased quantitatively. Therefore, if all SO3(g) generated by the thermal decomposition of alunite reacts with CaCO3 (or CaO, the thermal decomposition product of limestone) to form CaSO4 in an alunite- limestone system, 1 mol of pure alunite reacts with 6 mol of limestone to form 1 mol of 3CaO·3Al2O3·CaSO4 and 1 mol of 2CaSO4·K2SO4.

Performance improvement of local Korean natural hydraulic lime-based mortar using inorganic by-products

Our goal was to verify the manufacturing availability of local Korean natural hydraulic lime (K-NHL) using local Korean low-grade limestone and to test the basic physical properties on the basis of EU standards (BS EN 459-1:2015). We also sought to improve the physical properties of natural hydraulic lime by adding inorganic by-products such as blast furnace slag and silica fume. Where the inorganic by-products were not incorporated, properties such as soundness, air content, particle size, and water absorption (excluding compressive strength and setting time) did not show significant differences with the physical properties evaluated based on EU standards. Also, in terms of the composition of hydraulic phase, local Korean NHL A5 and A8 were similar to NHL 2 of EU standards, whereas local Korean NHL HL correlated with NHL 3.5 or NHL 5. When inorganic by-products were added, the compressive strength and setting time were improved.

Influence of Physicochemical Characteristic of Donghae-Samcheok Limestones on the Performance of Flue Gas Desulfurization (FGD)

It studies that effect of limestone of physicochemical characteristic on the performance of flue gas desulfurization (FGD) and application examination for technology of wet type FGD process and to utilize the limestone in Donghae-Samcheok. The experiment method was measured total neutralizing capability (TNC) using the lab scale experimental apparatus based on the HCl titration test. The results of TNC of limestone samples were more dependent on the physical characteristics including particle size rather than chemical compositions such as CaO content and particle size of limestone get smaller, TNC is increased.