Electroless Ni-P Deposition on Magnesium Alloy from a Sulfate Bath

A technology for electroless Ni-P deposition on AZ91D from a low cost plating bath containing sulfate nickel was proposed. The seal pretreatment was employed before the electroless Ni-P deposition for the sake of occluding the micro holes of the cast magnesium alloy and interdicting the bubble formation in the Ni-P coating during plating process. And pickling pretreatment can provide a better adhesion between the Ni-P deposition and AZ91D substrate. The deposition speed of the Ni-P coating is 29 μm/h. The technology is employed to AZ91D magnesium alloy automobile parts and can provide high hardness and high wear-resistant. The weight losses of Ni-P plated and heat-treated Ni-P plated magnesium alloy specimen are only about 1/6 and 1/10 that of bare magnesium alloy specimen after 10 min abrasion wear, respectively. The hardness of the electroless Ni-P plated brake pedal support brackets is 674.1 VHN and 935.7 VHN after 2 hours heat treatments at 180 °. The adhesion of Ni-P coatings on magnesium alloy substrates meets the demands of ISO Standards 2819. The technology is environment friendly and cannot cause hazard to environment because of absence of chromate in the whole process.

Study of hypoxia-induced expression of HIF-1α in retina pigment epithelium

It was shown that the expression of HIF-1α in retinal pigment epithelium increased under hypoxic conditions. Eight hours after the start of hypoxic exposure, the expression of HIF-1α reached the peak and sustained after 24-hour hypoxia. However, the morphology of PRE cells began to change and the expression of HIF-1α decreased after long-term (48-hour) hypoxia. Hypoxia-induced increase in the level of HIF-1α in RPE. It can be an important step in choriodal neovascularization.