Synthesis and photoluminescence of CdS QDs in ZrO2 nanotubes by sequential chemical bath deposition

Highly ordered ZrO2 nanotube (NT) arrays were fabricated by anodization in organic electrolyte containing NH4F. A facile sequential-chemical bath deposition technique was used to prepare CdS quantum dots (QDs) in the pores of ZrO2 NTs. XRD and HRTEM results confirmed the formation of single-phase wurtzite CdS nanoparticles with uniform size around 10 nm. UV–vis absorption and photoluminescence spectra proved that the CdS QD coating strongly enhanced the photon absorption of the NT arrays, as well as their PL signals in the visible broadband section which mostly arose from structure-dependent defects and oxygen vacancies in the nanohybrid layers.

Template-based synthesis and magnetic properties of Mn-Zn ferrite nanotube and nanowire arrays

Template-based electrophoretic deposition of Mn-Zn ferrite nanotubes (NTs) and nanowires (NWs) were achieved using anodic alumina oxide (AAO) membranes. The effect of electrophoretic current and deposition time on the morphology of the tubes was investigated. The samples show cubic spinel structure with no preferred orientation. Room-temperature magnetic properties of the Mn-Zn ferrite NT/NW arrays were studied. The magnetic easy axis parallels the NT/NW’s channel axis attributing to the large shape anisotropy in this direction, especially for the NTs with a small wall thickness. Magnetocrystalline anisotropy and magnetostatic interactions were found dominant in the samples when applied field was perpendicular to the channel axis.