Lina Zhong

Gold@Polymer Nanostructures with Tunable Permeability Shells for Selective Catalysis

National Natural Science Foundation of China [50873082, 50903067]; Scientific and Technical Project of Fujian Province of China [2009J1009, 2010H6021]

Preparation, characterization, and antibacterial activity studies of silver-loaded poly(styrene-co-acrylic acid) nanocomposites

A simple method for preparing a new type of stable antibacterial agent was presented. Monodisperse poly(styrene-co-acrylic acid) (PSA) nanospheres, serving as matrices, were synthesized via soap-free emulsion polymerization. Field-emission scanning electron microscopy micrographs indicated that PSA nanospheres have interesting surface microstructures and well-controlled particle size distributions. Silver-loaded poly(styrene-co-acrylic acid) (PSA/Ag-NPs) nanocomposites were prepared in situ through interfacial reduction of silver nitrate with sodium borohydride, and further characterized by transmission electron microscopy and X-ray diffraction. Their effects on antibacterial activity including inhibition zone, minimum inhibitory concentration (MIC), minimum bactericidal concentration (MBC), and bactericidal kinetics were evaluated. In the tests, PSA/Ag-NPs nanocomposites showed excellent antibacterial activity against both gram-positive Staphylococcus aureus and gram-negative Escherichia coli. These nanocomposites are considered to have potential application in antibacterial coatings on biomedical devices to reduce nosocomial infection rates.

Heterogeneous silver-polyaniline nanocomposites with tunable morphology and controllable catalytic properties.

This paper introduces not only a simple hydrothermal route to silver-polyaniline (Ag-PANI) nanocomposites with controllable morphology, but also a type of catalyst possessing tunable and switchable catalytic capability. Ag-PANI Janus nanoparticles (NPs) and Ag@PANI core-shell NPs have been constructed successfully at different hydrothermal temperatures. The diameter of both Ag and PANI hemispheres of Janus NPs, as well as the PANI shell thickness of core-shell NPs, was finely tuned via adjustment of the feed ratio. We also gained a deeper insight into the functionalities of PANI components in the catalytic capability of the heterogeneous catalysts, choosing catalytic reductions of nitrobenzene (NB) and 4-nitrophenol (4-NP) as model reactions. Our results showed that the catalytic capability of the nanocomposites was dependent on the PANI morphology and hydrophobicity. The PANI shell coating on Ag NPs can concentrate the lipophilic NB, thus leading to an enhanced catalytic capability of Ag@PANI core-shell NPs. However, this enhanced catalytic capability was not observed for Ag-PANI Janus NPs when catalytically reducing NB. More importantly, the catalytic capability of the core-shell NPs in the reduction of hydrophilic 4-NP is switchable by varying the PANI shell from an undoped to a doped state.

Three-dimensional gold nanodendrimers: never conglomerating nanocatalyst

3D Au nanodendrimers constructed by radially arranged thin nano-sheets show tunable morphology and diameter. The unexpectedly large specific surface area resulting from the novel porous nanostructure makes the 3D Au nanodendrimers exhibit high catalytic activity and long service life.