Lourenço Correr Sobrinho

Effect of etching and airborne particle abrasion on the microstructure of different dental ceramics

STATEMENT OF PROBLEM The ceramic composition and microstructure surface of all-ceramic restorations are important components of an effective bonding substrate. Both hydrofluoric acid etching and airborne aluminum oxide particle abrasion produce irregular surfaces necessary for micromechanical bonding. Although surface treatments of feldspathic and leucite porcelains have been studied previously, the high alumina-containing and lithium disilicate ceramics have not been fully investigated. PURPOSE The purpose of this study was to assess the surface topography of 6 different ceramics after treatment with either hydrofluoric acid etching or airborne aluminum oxide particle abrasion. MATERIAL AND METHODS Five copings each of IPS Empress, IPS Empress 2 (0.8 mm thick), Cergogold (0.7 mm thick), In-Ceram Alumina, In-Ceram Zirconia, and Procera (0.8 mm thick) were fabricated following the manufacturers instructions. Each coping was longitudinally sectioned into 4 equal parts by a diamond disk. The resulting sections were then randomly divided into 3 groups depending on subsequent surface treatments: Group 1, specimens without additional surface treatments, as received from the laboratory (control); Group 2, specimens treated by use of airborne particle abrasion with 50-microm aluminum oxide; and Group 3, specimens treated with 10% hydrofluoric acid etching (20 seconds for IPS Empress 2; 60 seconds for IPS Empress and Cergogold; and 2 minutes for In-Ceram Alumina, In-Ceram Zirconia, and Procera). RESULTS Airborne particle abrasion changed the morphologic surface of IPS Empress, IPS Empress 2, and Cergogold ceramics. The surface topography of these ceramics exhibited shallow irregularities not evident in the control group. For Procera, the 50-microm aluminum oxide airborne particle abrasion produced a flattened surface. Airborne particle abrasion of In-Ceram Alumina and In-Ceram Zirconia did not change the morphologic characteristics and the same shallows pits found in the control group remained. For IPS Empress 2, 10% hydrofluoric acid etching produced elongated crystals scattered with shallow irregularities. For IPS Empress and Cergogold, the morphologic characteristic was honeycomb-like on the ceramic surface. The surface treatment of In-Ceram Alumina, In-Ceram Zirconia, and Procera did not change their superficial structure. CONCLUSION Hydrofluoric acid etching and airborne particle abrasion with 50-microm aluminum oxide increased the irregularities on the surface of IPS Empress, IPS Empress 2, and Cergogold ceramics. Similar treatment of In-Ceram Alumina, In-Ceram Zirconia, and Procera did not change their morphologic microstructure.

Effect of the increase of energy density on knoop hardness of dental composites light-cured by conventional QTH, LED and xenon plasma arc

The aim of this study was to evaluate the effect of the increase of energy density on Knoop hardness of Z250 and Esthet-X composite resins. Cylindrical cavities (3 mm in diameter X 3 mm in depth) were prepared on the buccal surface of 144 bovine incisors. The composite resins were bulk-inserted and polymerized using different light-curing units and times: conventional QTH (quartz-tungsten-halogen; 700 mW/cm(2); 20 s, 30 s and 40 s); LED (light-emitting diode; 440 mW/cm(2); 20 s, 30 s and 40 s); PAC (xenon plasma arc; 1700 mW/cm(2); 3 s, 4.5 s and 6 s). The specimens were stored at 37 degrees C for 24 h prior to sectioning for Knoop hardness assessment. Three measurements were obtained for each depth: top surface, 1 mm and 2 mm. Data were analyzed statistically by ANOVA and Tukeys test (p<0.05). Regardless of the light source or energy density, Knoop hardness of Z250 was statistically significant higher than that of Esthet-X (p<0.05). Specimens cured with PAC had lower hardness than those cured with QTH and LED (p<0.05). Higher Knoop hardness was obtained when the energy density was increased for LED and PAC (p<0.05). No statistically significant differences (p>0.05) were found for QTH. Knoop hardness values decreased with the increase of depth. The increase of energy density produced composites with higher Knoop hardness means using LED and PAC.

Comparative study of the dental substrate used in shear bond strength tests

The purpose of this study was to compare shear bond strength values obtained in human enamel and dentin with the values obtained in bovine teeth using two adhesive systems with different actions. Forty human tooth half-crowns and forty bovine tooth crowns were flattened to a minimum plain area of 5 mm in diameter. The samples were divided in four groups of 20 specimens each: 1) human enamel; 2) bovine enamel; 3) human dentin; 4) bovine dentin. The samples of each group were divided in 2 subgroups of 10 samples each, according to the adhesive system used: 1) Scotchbond Multi-Purpose (SBMP); and 2) Clearfil Liner Bond 2V (CLB2V) applied according to the manufacturers recommendations. Afterwards, restorations of Z100 composite with cylindrical shape (4 mm diameter x 5 mm height) were made using a metallic mold to submit the samples to shear bond testing on an Instron universal testing machine, at a crosshead speed of 0.5 mm/min. The data were submitted to ANOVA and Tukeys test (5%). In enamel, there was no statistical difference between bovine and human teeth for SBMP (7.36 MPa, human; 8.24 MPa, bovine), nor for CLB2V (10.01 MPa, human; 7.95, bovine). In dentin, SBMP showed a statistically lower mean on human dentin (7.01 MPa) than on bovine dentin (11.74 MPa). For CLB2V, there was no statistical difference between human (7.43 MPa) and bovine (9.27 MPa) substrates.

Correlation between light intensity and exposure time on the hardness of composite resin

This study evaluated the correlation between light intensity emitted by the curing units and exposure time on the of degree polymerization of dental composites by measured Knoop hardness. Specimens with 5 mm diameter and 2 mm height were prepared in a copper mold, covered with a mylar strip and polymerized for 30 sec by curing units with 50, 130, 180, 220, 280 and 520 mW/cm2, respectively. The output for all units was measured using a Curing Radiometer (Demetron). Other specimens were polymerized for 45, 60, 75, 90, 105, 120, 135, 150, 165 and 180 sec utilizing units of 130, 220 and 280 mW/cm2. Knoop hardness values of the top and bottom surfaces were measured after 24 h. The results indicate that the curing units with higher light intensity presented improved values of Knoop hardness on the top and bottom regions. As expected, the top surface always presented improved Knoop hardness values in relation to the bottom, after exposure for 30 sec. The values obtained on the surface were statistically superior compared to the values on the bottom (p<0.05) for the intensity of 130, 220 and 280 mW/cm2 after 30, 45 and 60 sec of exposure. ©2000 Kluwer Academic Publishers

The influence of 30-day-old Streptococcus mutans biofilm on the surface of esthetic restorative materials : An in vitro study

OBJECTIVE To evaluate the effects of Streptococcus mutans biofilm/restorative materials interaction on surface roughness, hardness and morphology of materials tested. METHODS Empress 2 (E2), Filtek Supreme (FS), Vitremer (V) and Ketac Molar Easymix (KM) were tested. Twenty-five disks of each material were made and divided into three storage groups: (1) 100% relative humidity (n=5); (2) growth medium (BHI and 1% sucrose) (n=5); (3) S. mutans biofilm-growth medium (n=15). Before storage, hardness measurements were immediately obtained from group 1 specimens. After 30 days of storage, the specimens were cleaned in order to obtain the surface roughness and hardness values, besides morphology analysis by scanning electron microscopy. RESULTS The surface roughness and hardness values obtained from E2 and FS specimens did not present statistically significant differences among the groups 1, 2 and 3 and between immediate and 30-day-old specimens of each material. However, group 3 specimens of V and KM showed statistically significant higher surface roughness means than other groups. Group 1 specimens of V and KM also showed higher hardness values than the immediate values. Group 3 specimens of V presented decreased hardness values compared with other groups. The scanning electron micrographs showed an increase in surface degradation from group 1 to group 3 for FS, V and KM. CONCLUSIONS Thirty-day-old biofilm promotes a negative effect on the surface morphology of FS, V and KM, on the surface roughness of V and KM and on the hardness of V.

Fracture Loads of All‐Ceramic Crowns under Wet and Dry Fatigue Conditions

PURPOSE The aim of this study was to test the hypothesis that fracture loads of fatigued dental ceramic crowns are affected by testing environment and luting cement. MATERIALS AND METHODS One hundred and eighty crowns were prepared from bovine teeth using a lathe. Ceramic crowns were prepared from three types of ceramic systems: an alumina-infiltrated ceramic, a lithia-disilicate-based glass ceramic, and a leucite-reinforced ceramic. For each ceramic system, 30 crowns were cemented with a composite resin cement, and the remaining 30 with a resin-modified glass ionomer cement. For each ceramic system and cement, ten specimens were loaded to fracture without fatiguing. A second group (n = 10) was subjected to cyclic fatigue and fracture tested in a dry environment, and a third group (n = 10) was fatigued and fractured in distilled water. The results were statistically analyzed using one-way ANOVA and Tukey HSD test. RESULTS The fracture loads of ceramic crowns decreased significantly after cyclic fatigue loading (p<or= 0.05); furthermore, fracture loads of crowns fatigued in a wet environment were statistically lower than those in a dry environment (p < 0.05). Crowns luted with a composite resin cement showed statistically greater fracture loads than those luted with a resin-modified glass ionomer cement (p<or= 0.05). CONCLUSIONS Fracture load of the three ceramic systems was found to be influenced by ceramic composition. Moreover, cement and fatigue condition influenced the fracture loads of the crown specimens evaluated in this study.

Evaluation of depth of cure and knoop hardness in a dental composite photo-activated using different methods

The aim of this study was to evaluate the depth of cure and Knoop hardness in the P60 composite resin photo-activated using different methods. A bipartite brass matrix (3 mm in diameter X 11 mm in height) was filled with the composite and photo-activation was performed using continuous light, exponential light, intermittent light, plasma arc curing (PAC) or light-emitting diodes (LED). After opening the matrix, the uncured material was removed with a steel spatula and the polymerized composite was measured using a pachymeter. The specimens were then included in self-curing acrylic resin and worn longitudinally and the hardness was measured on the surface and at depths of 1, 2, 3, 4 and 5 mm. The data were analyzed by ANOVA and Tukeys test (5%). The results showed that the depth of cure was higher with the intermittent light, followed by continuous light, exponential light, PAC and LED methods. Up to a depth of 2 mm, all methods revealed similar hardness values, but there were differences between them at other depths, at which LED demonstrated the lowest values followed by PAC.

Effect of resin liners on the microleakage of class V dental composite restorations

PURPOSE The aim of this study was to evaluate the effect of an adhesive applied in layers of different thickness or in association with a filled adhesive or with a low viscosity composite liner on the microleakage of composite restorations. METHODS Forty bovine incisors were prepared with round cavities (4mm diameter X 2mm depth) on the cementoenamel junction. The teeth were assigned to four groups according to the liner used: 1 (control) - application of 1 layer of the Scotchbond Multi Purpose adhesive system (SBMP); 2 - application of 3 layers of SBMP; 3 - application of 1 layer of SBMP followed by application of one layer of Optibond FL adhesive; 4 - application of one layer of SBMP followed by application of flowable composite Flow-it. All cavities were restored using composite resin Z100. The microleakage test was conducted according to ISO (TR11405). Data were analyzed by Kruskall-Wallis test (a=0.05). RESULTS Group 4 showed less leakage than Group 1. Groups 2 and 3 showed intermediate values and there were no statistical differences when they were compared to the values of Groups 1 and 4 CONCLUSION The use of resin liners with flowable composites can reduce the microleakage of composite restorations.

Effects of Horizontal Misfit and Bar Framework Material on the Stress Distribution of an Overdenture-Retaining Bar System: A 3D Finite Element Analysis

PURPOSE To evaluate the influence of horizontal misfit change and bar framework material on the distribution of static stresses in an overdenture-retaining bar system using finite element (FE) analysis. MATERIALS AND METHODS A 3D FE model was created including two titanium implants and a bar framework placed in the anterior part of a severely resorbed jaw. The model set was exported to mechanical simulation software, where horizontal displacement (10, 50, 100, and 200 μm) was applied simulating the settling of the framework, which suffered shrinkage during laboratory procedures. Four bar materials (gold alloy, silver-palladium alloy, commercially pure titanium, and cobalt-chromium alloy) were also simulated in the analysis using 50 μm as the horizontal misfit. Data were qualitatively evaluated using von Mises stress, given by the software. RESULTS The misfit amplification presented a great increase in the stress levels in the inferior region of the bar, screw-retaining neck, cervical and medium third of the implant, and cortical bone tissue surrounding the implant. The higher stiffness of the bar presented a considerable increase in the stress levels in the bar framework only. CONCLUSION The levels of static stresses seem to be closely linked with horizontal misfit, such that its amplification caused increased levels of stress in the structures of the overdenture-retaining bar system. On the other hand, the stiffness of the bar framework presented a lower effect on the static stress levels.

Influence of casting methods on marginal and internal discrepancies of complete cast crowns

The relationship between the application of die-spacer prior to wax pattern fabrication and metal removal from the inner surface of the casting on marginal and internal discrepancies of complete cast crowns was evaluated. One hundred and twenty complete crowns were cast with palladium-silver alloy melted by gas-oxygen torch or electrical resistance and cast with a centrifuge casting machine. After casting, the crowns were seated on each type of different marginal configuration dies (90-degree shoulder, 20-degree beveled shoulder, and 45-degree chamfered shoulder) with a static load of 90 N during 1 min. Evaluation of the marginal fit of the specimens was made using a digital micrometer. The crowns were embedded in acrylic resin and longitudinally sectioned to verify the internal discrepancy that occurred in lateral and occlusal interfaces with a digital micrometer. The data were submitted to ANOVA and Tukeys test with a significance level of 5%. The best marginal and inner fits were obtained with the gas-oxygen torch source. The 45-degree chamfered shoulder showed the best marginal and inner fit, and better internal relief was obtained in the crowns abraded with 50 microm Al2O3 particles.