Double acid etching treatment of dental implants for enhanced biological properties

Background: The topographical features on the surface of dental implants have been considered as a critical parameter for enhancing the osseointegration of implants. In this work, we proposed a surface obtained by a combination of shot blasting and double acid etching. The double acid etching was hypothesized to increase the submicron topography and hence further stimulate the biological properties of the titanium implant. Methods: The topographical features (surface roughness and real surface area), wettability and surface chemical composition were analyzed. Results: The results showed that the proposed method produced a dual roughness, mainly composed of randomly distributed peaks and valleys with a superimposed nanoroughness, and hence with an increased specific surface area. Despite the fact that the proposed method does not introduce significant chemical changes, this treatment combination slightly increased the amount of titanium available on the surface, reducing potential surface contaminants. Furthermore, the surface showed increased contact angle values demonstrating an enhanced hydrophobicity on the surface. The biological behavior of the implants was then assessed by culturing osteoblast-like cells on the surface, showing enhanced osteoblast adhesion, proliferation and differentiation on the novel surface. Conclusions: Based on these results, the described surface with dual roughness obtained by double acid etching may be a novel route to obtain key features on the surface to enhance the osseointegration of the implant. Our approach is a simple method to obtain a dual roughness that mimics the bone structure modified by osteoclasts and increases surface area, which enhances osseointegration of dental implants.

Characterisation of Laser Modified WC‐CoCr Coatings

In this work the affects of laser characteristics on surface morphology, microstructure, microhardness and wear rates of high velocity oxygen fuel (HVOF) WC–CoCr coatings were investigated. Continuous and pulsed laser treatments were applied on the HVOF coatings using a CO2 laser of 10.6 μm wavelength. Continuous laser treatment significantly improved homogeneity of the coatings. Pulsed laser treatment produced significantly higher discontinuities compared to continuous mode. Microhardness increased by 45% for continuous mode laser modified WC-CoCr coatings. However, wear resistance deteriorated, with a notable 40% increase in wear rate. The variations in coating properties were attributed to the re-melting and rapid quenching of the CoCr bonding matrix allowing for WC redistribution.