Marcelo Giannini

Indirect Restoration Thickness and Time after Light-Activation Effects on Degree of Conversion of Resin Cement

This study evaluated the effects of indirect restorative materials, curing conditions and time on the degree of conversion (DC) of a dual-cured resin cement using infrared spectroscopy. The resin cement (RelyX Unicem 2, 3M ESPE) was applied to the diamond surface of a horizontal attenuated-total-reflectance unit and activated using one of following conditions: self-cure, direct light exposure, light exposure through indirect restorative materials (resin nano-ceramic: Lava Ultimate, 3M ESPE or feldspathic ceramic: Vita Blocks Mark II, Vita Zahnfabrik). Four thicknesses (0.5, 1.0, 1.5 or 2.0 mm) of each indirect material were analyzed, and the light-activation was performed using a blue LED light. Data (n=5) were analyzed by three-way ANOVA, Tukeys post hoc and Dunnetts tests (α=5%). No significant differences in DC were observed between indirect materials of similar thickness. All groups exhibited higher DC after 10 min than after 5 min. At both times points, the self-cure group exhibited significantly lower DC than all the light exposure groups. Only when the overlying indirect restoration had a thickness of 2 mm did DC decrease significantly. The presence of a thick, indirect restoration can decrease the DC of resin cement. DC after 10 min was higher than after 5 min. The self-cure mode yielded lower DC than the light-activating one.

Potência Radiante, Irradiância e Espectro de Emissão de 22 Fontes de Fotoativação Utilizadas no Brasil

O trabalho mediu a potencia radiante, a irradiância e o espectro de emissao de 22 LCUs do mercado brasileiro. Foi medida a area das pontas (cm2) para calcular a irradiância a partir da potencia radiante (mW), que foi obtida por um medidor de potencia laser do laboratorio. O MARC- Patient Simulator (MARC- PS) com espectrometro de grau (USB4000, Ocean Optics) foi utilizado para medir o espectro no sensor anterior e posterior. Os dados foram analisados utilizando ANOVA two-way e os dados da potencia radiante foram analisados por ANOVA one-way seguida pelo teste de Tukey (a 0,05). Valo, Bluephase G2, Radii Plus mostrou irradiância semelhante na regiao anterior e posterior e ambos receberam irradiância maior que 500 mW / cm2. Seis LCUs apresentaram menor irradiância que a recomendada (500mW / cm2) quando usado na regiao posterior, KON-LUX, Altlux II, Biolux Standard, TL-01, Optilux 501, DX Turbo LED 1200 e duas LCUs quando foram usadas na regiao anterior KON-LUX e Altlux II. O Bluephase G2xa0 e Optilight Max forneceram a maior potencia e o KON-LUX, o Altlux II eo Biolux Standard mostraram as menores potencias. O espectro das LCUs de pico unico foi muito variavel e das multi-picos emitiram espectro semelhante para ambos os sensores. O design, a potencia radiante, a irradiância e o tipo de LCUs sao fatores que os clinicos e pesquisadores precisam ter dominio quando necessitam fotoativar materiais resinosos. Palavras-chave: Fontes de Luz. Potencia. Irradiância. Espectro de Emissao no Simulador de Paciente de MARC.

Efeitos de unidades fotoativadoras e da escovação nas superfícies de compósitos do tipo

Resumo Este estudo avaliou os efeitos de unidades fotoativadoras e da escovação na perda de volume (PV), perfil de rugosidade (PR), rugosidade superficial (RS), morfologia (MO) e microdureza (MI) de compósitos do tipo “bulk-fill”. Os aparelhos fotoativadores (Valo e Demi Ultra) foram utilizados para polimerizar três compósitos: Filtek Bulk Fill Posterior Restorative (FBF), Tetric EvoCeram Bulk Fill (TET) e Surefil SDR Flow (SDR). Discos dessas resinas compostas foram preparados (n = 10) e submetidos à escovação (30.000 ciclos). Posteriormente, foram analisados em microscópio confocal para determinar a PV, PR, RS e MO. A MI foi analisada em microdurômetro e a MO também foi avaliada em microscopia eletrônica de varredura. Os dados foram analisados por teste T-pareado (RS), ANOVA de dois (PV e PR), três fatores (MI) e teste de Tukey (α = 0,05).

Estudo da Resistência de União à Dentina de Adesivos Auto-Condicionantes

Resumo O objetivo desse estudo foi avaliar a resistência de união de 5 sistemas adeivos auto-condicionantes (Clearfil SE Bond, Kuraray Noritake Dental Inc.; Clearfil SE Bond 2, Kuraray Noritake Dental Inc.; G-Premio BOND, GC Corp.; Bond Force II, Tokuyama Dental Corp; e Tetric N-Bond Universal, Ivoclar Vivadent) à superfície dentinária. Para isso, a superície dentinária de 40 terceiros molares humanos foi exposta e os dentes restaurados confome a recomendação dos fabricantes de cada sistema adesivo. Os dentes restaurados foram seccionados e os espécimes foram obtidos para realizar o teste de microtração.