Márcio José Mendonça

Influence of different light curing units on the bond strength of indirect resin composite restorations.

The aim of this study was to evaluate the influence of different light sources on the bond strength of indirect resin composite restorations cemented with a dual-cure resin cement. The superficial dentin of human third molars was exposed and acid-etched and an adhesive system was applied (Single Bond 2). Four-mm-thick indirect resin composite restorations (Gradia) were fabricated and cemented using a dual-cure resin cement (Rely X). Four light sources were used to polymerize the cement: QTH - Optilux 401; LED1 - L.E.Demetron 1; LED2 - Optilight CL; and LED3--Ultralume 5. The teeth were stored for 24 h and then sectioned, yielding stick-shaped specimens for each group with a bonded area of 1.0 mm(2). The specimens were then tested in a universal testing machine, at a crosshead speed of 1 mm/min. Data were analyzed using ANOVA. Bond strength mean values were: QTH: 22.5 (+/- 8.4); LED1: 22.7 (+/- 9.4); LED2: 21.4 (+/- 10.2); and LED3: 27.3 (+/- 13.8). No statistically significant difference was observed among the experimental groups. The bond strength values when the cement was polymerized using different LED lights were equivalent to the values when the QTH light was used. It can be concluded that the variety of light sources used in the present study did not influence the bond strength of indirect resin composite restorations cemented with a dual-cure resin cement.

Influência do tipo de ponteira condutora de luz na microdureza de uma resina composta

O objetivo desta pesquisa foi avaliar a influencia do tipo de ponteira condutora de luz na microdureza de uma resina composta micro-hibrida. Foram confeccionados 14 corpos de prova da resina composta Opallis (FGM) com dimensoes: 5 x 2 mm, divididos em dois grupos de acordo com a ponteira condutora de luz do aparelho fotoativador de lâmpada halogena Optilight Plus - GNATUS/300 mW.cm-2. GI - ponteira condutora de luz de fibra optica; GII - ponteira condutora de luz de polimero. Apos 24 horas, as medidas de microdureza foram efetuadas com um microdurometro HMV 2000 (Shimadzu Japao). Cinco penetracoes foram efetuadas em cada superficie (topo e base) totalizando 10 penetracoes para cada corpo de prova. A analise estatistica dos resultados realizada por meio do teste de ANOVA nao apresentou diferencas significativas entre os tipos de ponta condutora de luz nas superficies avaliadas. A analise estatistica demonstrou diferenca significativa nos valores medios de microdureza superficial entre as superficies de topo e de base, para ambas as ponteiras. Com base nos resultados obtidos, foi possivel concluir que as ponteiras de luz nao interferem na microdureza da resina composta, e que ambas apresentaram diferencas estatisticamente significativas nos valores de microdureza das superficies topo e base.

Influência de três modos de fotopolimerização sobre a microdureza de três resinas compostas

Proper curing of composites is critical to obtaining good toughness able to withstand masticatory forces. The objective of this study was to evaluate the influence of curing techniques - conventional (CONV), Soft -start (SS) and Pulse delayed (PA) in microhardness of three composites. To make up the body-of - evidence were used composites Filtek Z350 (3M ESPE), Empress Direct (IvoclarVivadent) and P90 (3M ESPE). Nine experimental groups were obtained according to the polymerization technique and composite resin. Twenty -four hours after curing was performed Knoop microhardness test surfaces of base and top of each body - of - evidence. Thus, the values ​​obtained were subjected to the Kruskal Wallis test followed by Dunns test, p < 0.05. The effectiveness of the polymerization on the top surface of the composites tested was not affected by different modes of polymerization. The Empress Direct composite resin showed the lowest hardness values ​​for all modes of polymerization compared to other composites evaluated.

Avaliação da fluorescência das resinas compostas para esmalte e dentina de diferentes marcas comerciais

This study analyzes and comparatively evaluate, by a visual method, the fluorescence of the color A2 composite resins for both enamel and dentin from seven different commercial sources. We made fifty-two specimens of anterior/posterior composite resins. The specimens were obtained with a rigid and transparent acrylic matrix. The polymerization was done irradiating with the 3M Curing Light 2500, intensity of 600 mW cm–² for 40 s. The specimens were polished with Sof-Lex discs. A wooden box painted with flat black paint was used to avoid light reflection and other light sources and the experiment was conducted in a darkroom. Three calibrated and trained evaluators rated the degree of fluorescence of the specimens under the effect of ultraviolet light, and classified them according to their intensity. For each evaluator, the specimens were mixed and randomly arranged inside the box. For the evaluation of fluorescence between resin enamel and dentin, the Kruskal-Wallis test (p <0.05) was applied. The best resins in terms of fluorescence of enamel are Esthet X-HD, TPH, Z350 and Opallis and for dentin are Opallis and Evolu-X.

Avaliação da influência da solução de irrigação na resistência adesiva de um cimento resinoso

INTRODUCAO: A contaminacao do substrato dentinario pode interferir na qualidade de uniao entre materiais adesivos e o dente. OBJETIVO: Investigar a influencia de diferentes solucoes de irrigacao na resistencia de uniao de um cimento resinoso. MATERIAL E METODO: Foram selecionadas 40 coroas dentais bovinas, divididas em quatro grupos: G0 = soro; G1 = clorexidina; G2 = EDTA; G3 = clorexidina 0,12%, apos condicionamento acido. Em seguida, foram confeccionados cilindros de cimento resinoso utilizando-se uma matriz de Tygon com diâmetro interno de 1 mm e 2 mm de altura. A fotoativacao foi realizada por aparelho de luz LED com 900 mW/cm2 por 40 segundos. Foram confeccionados quatro cilindros de cimento resinoso para cada coroa bovina, totalizando 40 corpos de prova de cimento resinoso para cada grupo avaliado. O teste de resistencia adesiva por microcisalhamento foi realizado apos 24 horas. Decorrido esse periodo, os cilindros de cimento resinoso foram testados em uma maquina universal de ensaios (EMIC). Os dados obtidos foram submetidos a analise estatistica pelos testes ANOVA e Tukey (p = 0,001). RESULTADO: Nao houve diferencas estatisticamente significativas entre os grupos estudados, com excecao para o G3, que apresentou de forma significativa os menores valores de resistencia adesiva. CONCLUSAO: As diferentes solucoes irrigadoras utilizadas previamente ao condicionamento acido na dentina nao interferem na resistencia de uniao por microcisalhamento.