Maria Rita Ortega Vega

Anticorrosive performance of commercial nanoceramic coatings on AISI 1010 steel

The aim of this work was to study the corrosion behavior of three commercial nanoceramic coatings in comparison to zinc phosphate coatings applied on mild steel (SAE 1010). The coatings were evaluated by scanning electron microscopy (SEM), profilometry and hydrophobicity. The electrochemical behavior was evaluated by dynamic polarization. The results showed that the samples coated with nanoceramics presented contact angles greater than 100o, achieving hydrophobic behavior. Evaluating the electrochemical behavior under dynamic polarization revealed that the nanoceramic coating containing chromium (CHT) exhibited a higher corrosion potential and lower current than the other nanoceramic coatings tested, although its performance in a dilute sodium chloride solution was below that of the zinc phosphate-based coating. Although the nanoceramic coatings exhibited poor electrochemical behavior compared to the zinc-based coatings, they had a higher corrosion resistance when associated with an organic coating.

Effect of concentrations of plasticizers on the sol-gel properties developed from alkoxides precursors

Coatings developed through sol-gel method is presented as an interesting replacement to chromium coating. Sol-gel method present advantages as high purity and excellent distribution of the components. The objective of this work is to synthesize and characterize a film obtained by sol-gel route. The film was prepared with 3-(trimethoxysilylpropyl) methacrylate (TMSPMA), tetraethoxysilane (TEOS) and cerium nitrate, using water and ethanol as solvents. Polyethyleneglycol (PEG) plasticizer was added at four different concentrations. The sol was characterized by techniques of viscosity, thermogravimetric analysis (TGA), X-ray diffraction (XRD) nuclear magnetic resonance spectroscopy (NMR) and Fourier transform infrared spectroscopy (FT-IR). The results showed that tetrafunctional alkoxides condensation was retarded by the plasticizer, forming a compact film. The film with 20 g.L-1 of PEG showed the best electrochemical behavior.