Leaching Behavior of Salt Wastes Conditioned with Sodalite Blended with Two Different Glass Powders

Two different glass powders (a commercially available glass frit and a borosilicate glass) have been used as blending agents for sodalite, an aluminosilicate mineral able to condition chloride salt wastes from pyrometallurgical processes. The synthesis of the mineral phase has been made through a process recently proposed by Idaho National Laboratory in USA, starting from a homogeneous powder of nepheline, chloride salts and glass. The mix, put into an alumina crucible, was introduced in a furnace inside an argon-atmosphere glove-box. The furnace temperature was then raised to 925 C, where it was kept for 7 hours. Leach tests under static conditions, according to ASTM C1285-02, have then been carried out on the final waste forms at room temperature (23 C) and in an oven at 90 C. SEM investigations have also been made before and after leach tests, in order to check the status of the powders. In particular the effect of the leaching process on the surface of the sodalite grains at 90 C from 30 to 150 days has been evidenced. The results obtained in the present study have been usefully compared to those from a similar test on a sodalite added with a glass frit by Idaho National Laboratory. Financial support from the Nuclear Fission Safety Program of the European Union is gratefully acknowledged (project ACSEPT, contract FP7-CP-2007-211 267).

A New Matrix for Conditioning Chloride Salt Wastes from the Electrorefining of Spent Nuclear Fuel

A novel method proposed by Korea Atomic Energy Research Institute has been applied to the treatment of chloride salt wastes coming from electrorefining of spent nuclear fuel, which allows to separate uranium from fission products. It is based on a matrix, SAP (SiO2-Al2O3-P2O5), synthesized by a conventional sol-gel process, able to stabilize the volatile salt wastes due to the formation of metalaluminosilicates, metalaluminophosphates and metalphosphates. With this method a higher disposal efficiency and a lower waste volume can be obtained. Eutectic melt LiCl-KCl (59-41 mol%) has been used to simulate the waste salt. The composite SAP has been prepared by using tetraethyl ortosilicate (TEOS), aluminum chloride (AlCl3.6H2O) and phosphoric acid (H3PO4) as sources of Si, Al, and P, respectively. All reagents were dissolved in EtOH/H2O and the mixture, tightly sealed, was placed in an electric oven at 70 C. After a gelling/ageing for 3 days, the transparent hydrogels were dried at 110 C for 3 days and then thermally treated at 600 C for 2 hours. The final product (SAP) was reacted with metal chlorides at increasing temperatures for 20 hours inside an Argon-atmosphere glove-box, after mixing them at a SAP/metal chloride mixing ratio of 2. The obtained products have been characterized by means of density measurements, scanning electron microscopy, thermal analysis, as well as by XRD, FTIR and Raman spectra. Financial support from the Nuclear Fission Safety Program of the European Union (project SACSESS, contract FP7-CP-2012-323282) is gratefully acknowledged.