Meng Guolin

The effect of pore size on tissue ingrowth and neovascularization in porous bioceramics of controlled architecture in vivo.

The purpose of this study was to investigate the role of pore size on tissue ingrowth and neovascularization in porous bioceramics under the accurate control of the pore parameters. For that purpose, β-tricalcium phosphate (β-TCP) cylinders with four different macropore sizes (300-400, 400-500, 500-600 and 600-700 µm) but the same interconnection size (120 µm) and unchangeable porosity were implanted into fascia lumbodorsalis in rabbits. The fibrous tissues and blood vessels formed in scaffolds were observed histologically and histomorphometrically. The vascularization of the porous bioceramics was analyzed by single-photon emission computed tomography (SPECT). It is found that pore size as an important parameter of a porous structure plays an important role in tissue infiltration into porous biomaterial scaffolds. The amount of fibrous tissue ingrowth increases with the decrease of the pore size. In four kinds of scaffolds with different macropore sizes (300-400, 400-500, 500-600 and 600-700 µm) and a constant interconnection size of 120 µm, the areas of fibrous tissue (%) were 60.5%, 52.2%, 41.3% and 37.3%, respectively, representing a significant decrease at 4 weeks (P < 0.01). The pore size of a scaffold is closely related to neovascularization of macroporous biomaterials implanted in vivo. A large pore size is beneficial for the growth of blood vessels, and the diameter of a pore smaller than 400 µm limits the growth of blood vessels and results in a smaller blood vessel diameter.

Characterization of a rabbit osteoporosis model induced by ovariectomy and glucocorticoid

Background and purpose Experimental models of osteoporosis in rabbits are useful to investigate anabolic agents because rabbits have an active Haversian remodeling and achieve skeletal maturiaty quickly. In this study, an experimental model of osteoporosis in rabbits induced by a combination of ovariectomy and glucocorticoid was characterized to provide a useful model for prevention and therapy of osteoporosis. Methods 32 skeletally mature female rabbits were divided randomly into 4 groups: sham control, bilateral ovariectomy (OVX), 1mg/kg/day methylprednisolone (MP) for 8 weeks, and OVX in combination with MP. All rabbits were killed 10 weeks after surgery. Bone mineral density (BMD) of lumbar spine was measured by dual-energy X-ray absorptiometry at baseline, and at 6 and 10 weeks postoperatively. Bone microarchitecture and mechanical properties of lumbar vertebrae were investigated by high-resolution micro-computed tomography and compression test, respectively, after killing. Results Mean BMD of the OVX+MP group at 10 weeks was reduced by about 36% from baseline (p < 0.001). Bone microarchitecture of lumbar vertebrae in the OVX+MP group indicated osteoporosis-associated deterioration. There was a statistically significant reduction in maximum load, stiffness, and energy absorption capacity of lumbar vertebrae in the OVX+MP group, but not in the OVX group, compared to the sham control. In the MP group, BMD and some microarchitecture parameters such as trabecular thickness and bone volume fraction were reduced. The mechanical properties were not statistically significantly different from those in the sham control group, however, although a negative trend was observed. Interpretation Osteopenia can be induced experimentally in rabbits through a combination of OVX and MP, and can be evaluated by BMD, bone microstructure, and mechanical parameters.