In situ X-ray scattering evaluation of heat-induced ultrastructural changes in dental tissues and synthetic hydroxyapatite.

Human dental tissues consist of inorganic constituents (mainly crystallites of hydroxyapatite, HAp) and organic matrix. In addition, synthetic HAp powders are frequently used in medical and chemical applications. Insights into the ultrastructural alterations of skeletal hard tissues exposed to thermal treatment are crucial for the estimation of temperature of exposure in forensic and archaeological studies. However, at present, only limited data exist on the heat-induced structural alterations of human dental tissues. In this paper, advanced non-destructive small- and wide angle X-ray scattering (SAXS/WAXS) synchrotron techniques were used to investigate the in situ ultrastructural alterations in thermally treated human dental tissues and synthetic HAp powders. The crystallographic properties were probed by WAXS, whereas HAp grain size distribution changes were evaluated by SAXS. The results demonstrate the important role of the organic matrix that binds together the HAp crystallites in responding to heat exposure. This is highlighted by the difference in the thermal behaviour between human dental tissues and synthetic HAp powders. The X-ray analysis results are supported by thermogravimetric analysis. The results concerning the HAp crystalline architecture in natural and synthetic HAp powders provide a reliable basis for deducing the heating history for dental tissues in the forensic and archaeological context, and the foundation for further development and optimization of biomimetic material design.

X-ray scattering evaluation of ultrastructural changes in human dental tissues with thermal treatment.

Micro‐ and ultrastructural analysis of burned skeletal remains is crucial for obtaining a reliable estimation of cremation temperature. Earlier studies mainly focused on heat‐induced changes in bone tissue, while this study extends this research to human dental tissues using a novel quantitative analytical approach. Twelve tooth sections were burned at 400–900°C (30‐min exposure, increments of 100°C). Subsequent combined small‐ and wide‐angle X‐ray scattering (SAXS/WAXS) experiments were performed at the Diamond Light Source synchrotron facility, where 28 scattering patterns were collected within each tooth section. In comparison with the control sample, an increase in mean crystal thickness was found in burned dentine (2.8‐fold) and enamel (1.4‐fold), however at a smaller rate than reported earlier for bone tissue (5–10.7‐fold). The results provide a structural reference for traditional X‐ray scattering methods and emphasize the need to investigate bone and dental tissues separately to obtain a reliable estimation of cremation temperature.

Hierarchical modelling of in situ elastic deformation of human enamel based on photoelastic and diffraction analysis of stresses and strains

Human enamel is a typical hierarchical mineralized tissue with a two-level composite structure. To date, few studies have focused on how the mechanical behaviour of this tissue is affected by both the rod orientation at the microscale and the preferred orientation of mineral crystallites at the nanoscale. In this study, wide-angle X-ray scattering was used to determine the internal lattice strain response of human enamel samples (with differing rod directions) as a function of in situ uniaxial compressive loading. Quantitative stress distribution evaluation in the birefringent mounting epoxy was performed in parallel using photoelastic techniques. The resulting experimental data was analysed using an advanced multiscale Eshelby inclusion model that takes into account the two-level hierarchical structure of human enamel, and reflects the differing rod directions and orientation distributions of hydroxyapatite crystals. The achieved satisfactory agreement between the model and the experimental data, in terms of the values of multidirectional strain components under the action of differently orientated loads, suggests that the multiscale approach captures reasonably successfully the structure-property relationship between the hierarchical architecture of human enamel and its response to the applied forces. This novel and systematic approach can be used to improve the interpretation of the mechanical properties of enamel, as well as of the textured hierarchical biomaterials in general.

Structure-mechanical function relations at nano-scale in heat-affected human dental tissue

The knowledge of the mechanical properties of dental materials related to their hierarchical structure is essential for understanding and predicting the effect of microstructural alterations on the performance of dental tissues in the context of forensic and archaeological investigation as well as laser irradiation treatment of caries. So far, few studies have focused on the nano-scale structure-mechanical function relations of human teeth altered by chemical or thermal treatment. The response of dental tissues to thermal treatment is thought to be strongly affected by the mineral crystallite size, their spatial arrangement and preferred orientation. In this study, synchrotron-based small and wide angle X-ray scattering (SAXS/WAXS) techniques were used to investigate the micro-structural alterations (mean crystalline thickness, crystal perfection and degree of alignment) of heat-affected dentine and enamel in human dental teeth. Additionally, nanoindentation mapping was applied to detect the spatial and temperature-dependent nano-mechanical properties variation. The SAXS/WAXS results revealed that the mean crystalline thickness distribution in dentine was more uniform compared with that in enamel. Although in general the mean crystalline thickness increased both in dentine and enamel as the temperature increased, the local structural variations gradually reduced. Meanwhile, the hardness and reduced modulus in enamel decreased as the temperature increased, while for dentine, the tendency reversed at high temperature. The analysis of the correlation between the ultrastructure and mechanical properties coupled with the effect of temperature demonstrates the effect of mean thickness and orientation on the local variation of mechanical property. This structural-mechanical property alteration is likely to be due to changes of HAp crystallites, thus dentine and enamel exhibit different responses at different temperatures. Our results enable an improved understanding of the mechanical properties correlation in hierarchical biological materials, and human dental tissue in particular.

Multiscale modelling and diffraction-based characterization of elastic behaviour of human dentine

Human dentine is a hierarchical mineralized tissue with a two-level composite structure, with tubules being the prominent structural feature at a microlevel, and collagen fibres decorated with hydroxyapatite (HAp) crystallite platelets dominating the nanoscale. Few studies have focused on this two-level structure of human dentine, where the response to mechanical loading is thought to be affected not only by the tubule volume fraction at the microscale, but also by the shape and orientation distribution of mineral crystallites, and their nanoscale spatial arrangement and alignment. In this paper, in situ elastic strain evolution within HAp in dentine subjected to uniaxial compressive loading along both longitudinal and transverse directions was characterized simultaneously by two synchrotron X-ray scattering techniques: small- and wide-angle X-ray scattering (SAXS and WAXS, respectively). WAXS allows the evaluation of the apparent modulus linking the external load to the internal HAp crystallite strain, while the nanoscale HAp distribution and arrangement can be quantified by SAXS. We proposed an improved multiscale Eshelby inclusion model that takes into account the two-level hierarchical structure, and validated it with a multidirectional experimental strain evaluation. The agreement between the simulation and measurement indicates that the multiscale hierarchical model developed here accurately reflects the structural arrangement and mechanical response of human dentine. This study benefits the comprehensive understanding of the mechanical behaviour of hierarchical biomaterials. The knowledge of the mechanical properties related to the hierarchical structure is essential for the understanding and predicting the effects of structural alterations that may occur due to disease or treatment on the performance of dental tissues and their artificial replacements.

Volume analysis of heat-induced cracks in human molars: A preliminary study

Context: Only a few methods have been published dealing with the visualization of heat-induced cracks inside bones and teeth. Aims: As a novel approach this study used nondestructive X-ray microtomography (micro-CT) for volume analysis of heat-induced cracks to observe the reaction of human molars to various levels of thermal stress. Materials and Methods: Eighteen clinically extracted third molars were rehydrated and burned under controlled temperatures (400, 650, and 800°C) using an electric furnace adjusted with a 25°C increase/min. The subsequent high-resolution scans (voxel-size 17.7 μm) were made with a compact micro-CT scanner (SkyScan 1174). In total, 14 scans were automatically segmented with Definiens XD Developer 1.2 and three-dimensional (3D) models were computed with Visage Imaging Amira 5.2.2. The results of the automated segmentation were analyzed with an analysis of variance (ANOVA) and uncorrected post hoc least significant difference (LSD) tests using Statistical Package for Social Sciences (SPSS) 17. A probability level of P < 0.05 was used as an index of statistical significance. Results: A temperature-dependent increase of heat-induced cracks was observed between the three temperature groups (P < 0.05, ANOVA post hoc LSD). In addition, the distributions and shape of the heat-induced changes could be classified using the computed 3D models. Conclusion: The macroscopic heat-induced changes observed in this preliminary study correspond with previous observations of unrestored human teeth, yet the current observations also take into account the entire microscopic 3D expansions of heat-induced cracks within the dental hard tissues. Using the same experimental conditions proposed in the literature, this study confirms previous results, adds new observations, and offers new perspectives in the investigation of forensic evidence.

Hierarchical modelling of elastic behaviour of human enamel based on synchrotron diffraction characterisation

Human enamel is a hierarchical mineralized tissue with a two-level composite structure. Few studies have focused on the structure-mechanical property relationship and its link to the multi-scale architecture of human enamel, whereby the response to mechanical loading is affected not only by the rod distribution at micro-scale, but also strongly influenced by the mineral crystallite shape, and spatial arrangement and orientation. In this study, two complementary synchrotron X-ray diffraction techniques, wide and small angle X-ray scattering (WAXS/SAXS) were used to obtain multi-scale quantitative information about the structure and deformation response of human enamel to in situ uniaxial compressive loading. The apparent modulus was determined linking the external load and the internal strain in hydroxyapatite (HAp) crystallites. An improved multi-scale Eshelby model is proposed taking into account the two-level hierarchical structure of enamel. This framework has been used to analyse the experimental data for the elastic lattice strain evolution within the HAp crystals. The achieved agreement between the model prediction and experiment along the loading direction validates the model and suggests that the new multi-scale approach reasonably captures the structure-property relationship for the human enamel. The ability of the model to predict multi-directional strain components is also evaluated by comparison with the measurements. The results are useful for understanding the intricate relationship between the hierarchical structure and the mechanical properties of enamel, and for making predictions of the effect of structural alterations that may occur due to the disease or treatment on the performance of dental tissues and their artificial replacements.

Every-other-day feeding extends lifespan but fails to delay many symptoms of aging in mice

Dietary restriction regimes extend lifespan in various animal models. Here we show that longevity in male C57BL/6J mice subjected to every-other-day feeding is associated with a delayed onset of neoplastic disease that naturally limits lifespan in these animals. We compare more than 200 phenotypes in over 20 tissues in aged animals fed with a lifelong every-other-day feeding or ad libitum access to food diet to determine whether molecular, cellular, physiological and histopathological aging features develop more slowly in every-other-day feeding mice than in controls. We also analyze the effects of every-other-day feeding on young mice on shorter-term every-other-day feeding or ad libitum to account for possible aging-independent restriction effects. Our large-scale analysis reveals overall only limited evidence for a retardation of the aging rate in every-other-day feeding mice. The data indicate that every-other-day feeding-induced longevity is sufficiently explained by delays in life-limiting neoplastic disorders and is not associated with a more general slowing of the aging process in mice.Dietary restriction can extend the life of various model organisms. Here, Xie et al. show that intermittent periods of fasting achieved through every-other-day feeding protect mice against neoplastic disease but do not broadly delay organismal aging in animals.

Understanding nature's residual strain engineering at the human dentine-enamel junction interface.

UNLABELLED Human dental tissue is a hydrated biological mineral composite. In terms of volume and mass, a human tooth mainly consists of dentine and enamel. Human dental tissues have a hierarchical structure and versatile mechanical properties. The dentine enamel junction (DEJ) is an important biological interface that provides a durable bond between enamel and dentine that is a life-long success story: while intact and free from disease, this interface does not fail despite the harsh thermo-mechanical loading in the oral cavity. The underlying reasons for such remarkable strength and durability are still not fully clear from the structural and mechanical perspectives. One possibility is that, in an example of residual stress engineering, evolution has led to the formation of a layer of inelastic strain adjacent to the DEJ during odontogenesis (tooth formation). However, due to significant experimental and interpretational challenges, no meaningful quantification of residual stress in the vicinity of the DEJ at the appropriate spatial resolution has been reported to date. In this study, we applied a recently developed flexible and versatile method for measuring the residual elastic strain at (sub)micron-scale utilising focused ion beam (FIB) milling with digital image correlation (DIC). We report the results that span the transition from human dentine to enamel, and incorporate the material lying at and in the vicinity of the DEJ. The capability of observing the association between internal architecture and the residual elastic strain state at the micrometre scale is useful for understanding the remarkable performance of the DEJ and may help the creation of improved biomimetic materials for clinical and engineering applications. STATEMENT OF SIGNIFICANCE We studied the micron-scale residual stresses that exist within human teeth, between enamel (outer tooth shell, hardest substance in the human body) and dentine (soft bone-like vascularised tooth core). The dentine-enamel junction (DEJ) is an extremely interesting example of natures design in terms of hierarchical structuring and residual stress management. Key developments reported are systematic focused ion beam (FIB) milling and digital image correlation (DIC) micrometre scale residual strain evaluation, and the determination of principal strain direction near DEJ, correlated with internal architecture responsible for remarkable strength. This work helps understanding DEJ performance and improving biomimetic materials design for clinical and engineering applications.

Viable Ednra (Y129F) mice feature human mandibulofacial dysostosis with alopecia (MFDA) syndrome due to the homologue mutation.

Animal models resembling human mutations are valuable tools to research the features of complex human craniofacial syndromes. This is the first report on a viable dominant mouse model carrying a non-synonymous sequence variation within the endothelin receptor type A gene (Ednra c.386A>T, p.Tyr129Phe) derived by an ENU mutagenesis program. The identical amino acid substitution was reported recently as disease causing in three individuals with the mandibulofacial dysostosis with alopecia (MFDA, OMIM 616367) syndrome. We performed standardized phenotyping of wild-type, heterozygous, and homozygous EdnraY129F mice within the German Mouse Clinic. Mutant mice mimic the craniofacial phenotypes of jaw dysplasia, micrognathia, dysplastic temporomandibular joints, auricular dysmorphism, and missing of the squamosal zygomatic process as described for MFDA-affected individuals. As observed in MFDA-affected individuals, mutant EdnraY129F mice exhibit hearing impairment in line with strong abnormalities of the ossicles and further, reduction of some lung volumetric parameters. In general, heterozygous and homozygous mice demonstrated inter-individual diversity of expression of the craniofacial phenotypes as observed in MFDA patients but without showing any cleft palates, eyelid defects, or alopecia. Mutant EdnraY129F mice represent a valuable viable model for complex human syndromes of the first and second pharyngeal arches and for further studies and analysis of impaired endothelin 1 (EDN1)–endothelin receptor type A (EDNRA) signaling. Above all, EdnraY129F mice model the recently published human MFDA syndrome and may be helpful for further disease understanding and development of therapeutic interventions.