Influence of Ca2+ in Deicing Salt on the Corrosion Behavior of AM50 Magnesium Alloy

To lower the freezing point of deicing salt, calcium chloride (CaCl2) is commonly used. The influence of the presence and absence of the deicing salt ingredient Ca2+ on the corrosion behavior of die-cast AM50 magnesium alloy was investigated using an electrolyte close to the deicing salt composition with and without Ca2+ addition. The goal of the work was to point out the differences in the corrosion mechanism with and with-out Ca2+ addition by electrochemical investigations, H2 evolution, and weight-loss characterization. Under polarizing conditions the resulting current densities are significantly lower in the presence of Ca2+. Electrochemical impedance spectroscopy (EIS) measurements up to 4.5 h showed an increasing polarization resistance, RP, with time, and after 4.5 h, a breakdown of RP values in the presence of Ca2+ combined with the appearance of an inductive loop. Mass-gain, mass-loss, and hydrogen evolution measurements confirmed the inhibiting behavior in the presence of Ca2+ up to 1 day. Durin...

The Influence of Ca2+ in Deicing Salt on the Chemistry of Corrosion Products Formed on AM50 Magnesium Alloy—Calcareous Deposition

The corrosion inhibiting effect of Ca2+—which was presented in a previous publication of the authors under immersion conditions in the first 4.5 h—cannot be attributed to the incorporation of Ca2+ ...