Tunable photovoltaic performance of preferentially oriented rutile TiO 2 nanorod photoanodes based dye sensitized solar cells with quasi-state electrolyte

Photoanodes made of highly oriented TiO2 nanorod arrays with different aspect ratios were synthesized via one-step hydrothermal technique. Preferentially oriented single crystalline rutile TiO2 was confirmed by the single peak in XRD pattern (2θ=63o, (0 0 2)). FESEM image evidence the growth of an array of nanorods having different geometry with respect to reaction time and solution refreshment rate. The length, diameter and aspect ratio of the nanorods increased with reaction time as 4 hours (1.98 μm, 121 nm, 15.32), 8 hours (4 μm, 185 nm, 22.70), 12 hours (5.6 μm, 242 nm, 27.24) and 16 hours (8 μm, 254 nm, 38.02) respectively. Unlike conventional Dye-Sensitized Solar Cell (DSSC) with a liquid electrolyte, DSSC were fabricated here using 1D rutile TiO2 nanorods based photoanodes, N719 dye and quasi-state electrolyte. The charge transport properties were investigated from current-voltage curves and fitted using one-diode model. Interestingly photovoltaic performance of DSSCs increased exponentially with the length of the nanorod and is attributed to the higher surface to volume ratio, more dye anchoring, and channelized electron transport. Higher photovoltaic performance (Jsc=5.99 mA/cm2, Voc=750 mV, η=3.08%) was observed with photoanodes (16 hours) made of densely packed longest TiO2 nanorods (8 µm, 254 nm).