Effect of partial substitution of Ni by Co on the magnetic and magnetocaloric properties of Ni50Mn35In15 Heusler alloy

The magnetic and magnetocaloric properties of Ni48Co2Mn35In15 were studied using magnetization and heat capacity measurements. The magnetic entropy change (ΔSM) was evaluated from both magnetizing and demagnetizing fields. An inverse ΔSM for the magnetizing and demagnetizing processes were found to be 20.5 and 18.5 J kg−1 K−1, respectively, for ΔHu2009=u20095 T at the martensitic transition (Tu2009=u2009TM). The normal ΔSM was found to be −5.4 J kg−1 K−1 for both fields at the paramagnetic/ferromagnetic transition (Tu2009=u2009TC). The effective refrigeration capacity at TM and TC for magnetizing field was found to be 268 and 243 J/kg (285 and 243 J/kg for the demagnetizing field), respectively. We have also estimated the density of states, the Debye temperature, and the inverse adiabatic temperature change to be 4.93 states/eV f.u., 314 K, and −3.7 K, respectively, from the measured heat capacity data.