Paulo Afonso Silveira Francisconi

Diametral tensile strength and water sorption of glass-ionomer cements used in Atraumatic Restorative Treatment

The purposes of this study were to evaluate the diametral tensile strength and the water sorption of restorative (Fuji IX and Ketac Molar) and resin-modified glass-ionomer luting cements (ProTec Cem, Fuji Plus and Vitremer) mixed at both manufacturer and increased powder: liquid ratio, for their use in the Atraumatic Restorative Treatment. A conventional restorative glass-ionomer (Ketac Fil) was used as control. Specimens (6.0 mm in diameter x 3.0 mm in height) were prepared and stored (1 hour, 1 day and 1 week) for a diametral tensile strength test. Data were subjected to two-way ANOVA and Tukey tests (p<0.05). For the water sorption test, specimens of 15.0 mm in diameter x 0.5 mm in height were prepared and transfered to desiccators until a constant mass was obtained. Then the specimens were immersed in deionized water for 7 days, weighed and reconditioned to a constant mass in desiccators. Data were subjected to one-way ANOVA and Tukey tests (p<0.05). Five specimens of each studied material and consistency were prepared for each test. The resin-modified glass-ionomer cements showed significantly higher strength than the conventional materials. Except for ProTec Cem, the diametral tensile strength of the resin-modified materials significantly increased from luting to restorative consistency. Except for ProTec Cem, the water sorption of the resin-modified glass ionomers was higher than the others. The water sorption of resin-modified materials at restorative consistency was significantly lower than at luting consistency. Resin-modified glass-ionomer luting cements mixed at increased powder: liquid ratio showed better properties than at luting consistency.

Water sorption and solubility of different calcium hydroxide cements

Objectives: Calcium hydroxide cements have been largely used in deep cavities due to their abilities to stimulate dentin formation. However, their resistance can be relatively low and their solubility relatively high, in many instances. This study evaluated water sorption and solubility of different calcium hydroxide cements, in order to show alterations that may reduce their effectiveness. Material and methods: Five discs (20 mm in diameter and 1.5 mm thick) of three different materials (Biocal®, Dycal® and Hidro C®) were prepared with the aid of a ring-shaped metallic matrix. After being stored at 37°C for 24 h, the discs were weighed on a precision weight scale, dehydrated and weighed again. Immediately after weighing, discs were stored for a week in 50 mL of distilled water at 37°C and, then, weighed again, dehydrated and submitted to a new weighing. The loss of soluble material and its water sorption was obtained from the difference between the initial and the final dry mass of each disc, after 1 week of immersion in water. Data were analyzed for significant differences by two-way ANOVA and Tukeys test (p<0.05). Results: Mean water sorption values (g) ± standard deviation and percentage (%), for each evaluated cement, were: Biocal® (0.006 ± 0.001 / 2.15); Dycal® (0.016 ± 0.004 / 5.49); and Hidro C® (0.025 ± 0.003 / 8.27). Mean solubility values (g) ± standard deviation and percentage (%), for each evaluated cement, were: Biocal® (0.002 ± 0.001 / 0.72); Dycal® (0.013 ± 0.004 / 4.21); and Hidro C® (0.023 ± 0.004 / 7.65). Conclusions: Biocal® absorbed less water and was less soluble than the other evaluated cements; Hidro C® exhibited the highest water sorption and solubility values; and there were significant differences among all evaluated experimental groups.

The shear bond strength of self-adhesive resin cements to dentin and enamel: An in vitro study

STATEMENT OF PROBLEM Clinicians continue to search for ways to simplify bonding procedures without compromising clinical efficacy. PURPOSE The purpose of this study was to evaluate the shear strength of self-adhesive cements RelyX U100 and RelyX U200, and conventional resin cement RelyX ARC to enamel and dentin after different surface treatments. MATERIAL AND METHODS The crowns of 120 bovine incisor teeth were separated from the roots and embedded in epoxy resin in polyvinyl chloride tubes. In each tooth, the area to be cemented was delimited with central holed adhesive tape. The teeth were distributed into 12 groups (n=10) according to the substrate; etched or not with 37% phosphoric acid; and cement type of enamel-U100, enamel-phosphoric acid-U100, enamel-U200, enamel-phosphoric acid-U200, enamel-ARC, enamel-phosphoric acid-ARC, dentin-U100, dentin-phosphoric acid-U100, dentin-U200, dentin-phosphoric acid-U200, dentin-ARC, and dentin-phosphoric acid-ARC. After 7 days of storage in artificial saliva, shear strength tests were performed by using a universal testing machine (0.5 mm/min). The data were analyzed with 3-way ANOVA and the Tukey test (α=.05). Fracture analysis was performed with a light microscope. Two specimens from each group were analyzed with a scanning electron microscope. RESULTS In enamel, ARC (9.96 MPa) had higher shear strength (P=.038) than U100 (5.14 MPa); however, after surface etching, U100 (17.81 MPa) and U200 (17.52 MPa) had higher shear strength (P<.001). With dentin, no significant differences were observed (P=.999), except for dentin-ARC (0.34 MPa) (P=.001). Most fractures were of the adhesive type. CONCLUSIONS U200 self-adhesive cement had similar bond strength to the ARC in enamel, but the combination with phosphoric acid had the best bond strength. For dentin, self-adhesive resin cements are equally effective alternatives to conventional resin cement.

VOLUMETRIC POLYMERIZATION SHRINKAGE OF CONTEMPORARY COMPOSITE RESINS

The polymerization shrinkage of composite resins may affect negatively the clinical outcome of the restoration. Extensive research has been carried out to develop new formulations of composite resins in order to provide good handling characteristics and some dimensional stability during polymerization. The purpose of this study was to analyze, in vitro, the magnitude of the volumetric polymerization shrinkage of 7 contemporary composite resins (Definite, Suprafill, SureFil, Filtek Z250, Fill Magic, Alert, and Solitaire) to determine whether there are differences among these materials. The tests were conducted with precision of 0.1 mg. The volumetric shrinkage was measured by hydrostatic weighing before and after polymerization and calculated by known mathematical equations. One-way ANOVA (á=0.05) was used to determine statistically significant differences in volumetric shrinkage among the tested composite resins. Suprafill (1.87±0.01) and Definite (1.89±0.01) shrank significantly less than the other composite resins. SureFil (2.01±0.06), Filtek Z250 (1.99±0.03), and Fill Magic (2.02±0.02) presented intermediate levels of polymerization shrinkage. Alert and Solitaire presented the highest degree of polymerization shrinkage. Knowing the polymerization shrinkage rates of the commercially available composite resins, the dentist would be able to choose between using composite resins with lower polymerization shrinkage rates or adopting technical or operational procedures to minimize the adverse effects deriving from resin contraction during light-activation.

Effect of a metal primer on the bond strength of the resin-metal interface

To evaluate the effect of different surface treatments on shear bond strength between a metallic alloy (Co-Cr-Mo - Remanium CD) and a resin cement (Rely X TM) and to evaluate the mode of fracture after testing, forty couples of metallic-alloy disks were melted, regularized, polished, submitted to four thermal cycles (Vacuum, 960ºC, 8 minutes) and randomly separated into four groups. Each group received a different type of treatment: Group PSP: Polished with sandpaper 600; Group PCP: Polished with sandpaper 600 and application of the metal primer Alloy Primer (Kuraray); Group JSP: Sandblasted with 100µm aluminum oxide; Group JCP: Sandblasted with 100mm aluminum oxide and treated with a metal Primer. The groups were cemented and stored in distilled water at 37ºC for 36 hours and submitted to the shear bond strength test. The mean and standard deviation (in Kgf/cm²) obtained for each group was: PSP 4.0/0.4; PCP 88.9/33.6; JSP 163.2/27.6; JCP 144.5/54.0. After the statistical analysis the authors concluded that: the highest values were obtained for the sandblasted groups (JSP, JCP), regardless of the primer application; the Alloy Primer increased the retention between the Rely X cement and the polished surface of the Co-Cr-Mo alloy, yet its bond strength was not greater than that obtained with sandblasting; all specimens showed adhesive failures in the tested interface.