Surface topography and bacterial adhesion of CAD/CAM resin based materials after application of different surface finishing techniques

Aim: This study evaluated the surface topography and bacterial adhesion of a hybrid ceramic and a nano ceramic resin composite after different surface finishes. Methods: Hybrid ceramic (Vita Enamic, VITA - EN) and nano ceramic resin composite (Lava Ultimate, 3M/ESPE - LV) blocks of 12 x 14 x 18 mm were cut into 1 mm slices. Each slice was divided into four specimens (6 x 7 mm) that were randomly allocated into 4 groups (n=8) according to the surface finishing: CTL - without surface finish (control); DB - wear with a diamond bur; VT - polishing system for hybrid ceramic (VITA); and DD - polishing system for ceramics (Dedeco). The specimens were analyzed regarding surface roughness parameters (Ra, Rz, Rq), sterilized and subjected to bacterial adhesion. Representative specimens from each group were observed by SEM and Confocal Laser Scanning Microscopy. Data were submitted to two-way ANOVA and Tukeys test (α=0.05). Results: EN had lower surface roughness and bacterial adhesion than LV (p 0.05). The type of material and surface finish system significantly interfered with surface roughness parameters and bacterial adhesion. The hybrid ceramic performed better after polishing than the nano-ceramic resin. Conclusion: An adequate finishing/polishing technique should always be performed after any kind of adjustment to indirect restorations made with these materials tested.

Antibacterial Effect and Physical-Mechanical Properties of Temporary Restorative Material Containing Antibacterial Agents

Introduction. For the maintenance of the aseptic chain created during the treatment the coronal sealing becomes paramount. Aim. Evaluating the antibacterial effect and the physical-mechanical properties of a temporary restorative material containing different antibacterial agents. Material and Methods. Two antibacterial agents (triclosan and chloramine T) were manually added to a temporary restorative material used as base (Coltosol). The antibacterial action of the material was analyzed using the agar diffusion method, in pure cultures of Escherichia coli (ATCC BAA-2336) and Staphylococcus aureus (ATCC 11632) and mixed culture of saliva collection. The microleakage rate was analyzed using bovine teeth, previously restored with the materials, and submitted to thermocycling, in a solution of 0.5% methylene blue, for a period of 24 hours. The physical and mechanical properties of the materials analyzed were setting time, water sorption, solubility, and compression strength. Results. No marginal leakage was observed for all groups. There was no statistical significant difference in antimicrobial activity, setting time, water sorption, solubility, and compression strength among the materials. Conclusion. The addition of antibacterial agents on a temporary restorative material did not optimize the antibacterial ability of the material and also did not change its physical-mechanical properties.