Peter Heinl

Cellular Ti-6Al-4V structures with interconnected macro porosity for bone implants fabricated by selective electron beam melting.

Selective electron beam melting (SEBM) was successfully used to fabricate novel cellular Ti-6Al-4V structures for orthopaedic applications. Micro computer tomography (microCT) analysis demonstrated the capability to fabricate three-dimensional structures with an interconnected porosity and pore sizes suitable for tissue ingrowth and vascularization. Mechanical properties, such as compressive strength and elastic modulus, of the tested structures were similar to those of human bone. Thus, stress-shielding effects after implantation might be avoided due to a reduced stiffness mismatch between implant and bone. A chemical surface modification using HCl and NaOH induced apatite formation during in vitro bioactivity tests in simulated body fluid under dynamic conditions. The modified bioactive surface is expected to enhance the fixation of the implant in the surrounding bone as well as to improve its long-term stability.

Compression-compression fatigue of selective electron beam melted cellular titanium (Ti-6Al-4V).

Regular 3D periodic porous Ti-6Al-4V structures intended to reduce the effects of stress shielding in load-bearing bone replacement implants (e.g., hip stems) were fabricated over a range of relative densities (0.17-0.40) and pore sizes (approximately 500-1500 μm) using selective electron beam melting (EBM). Compression-compression fatigue testing (15 Hz, R = 0.1) resulted in normalized fatigue strengths at 10(6) cycles ranging from 0.15 to 0.25, which is lower than the expected value of 0.4 for solid material of the same acicular α microstructure. The three possible reasons for this reduced fatigue lifetime are stress concentrations from closed porosity observed within struts, stress concentrations from observed strut surface features (sintered particles and texture lines), and microstructure (either acicular α or martensite) with less than optimal high-cycle fatigue resistance.

In vivo performance of selective electron beam-melted Ti-6Al-4V structures.

Highly porous titanium structures are widely used for maxillofacial and orthopedic surgery because of their excellent mechanical properties similar to those of human bone and their facilitation of bone ingrowth. In contrast to common methods, the generation of porous titaniumproducts by selective electron beam melting (SEBM), an additive manufacturing technology, overcomes difficulties concerning the extreme chemical affinity of liquid titanium to atmospheric gases which consequently leads to strongly reduced ductility of the metal. The purpose of this study was to assess the suitability of a smooth compact and a porous Ti-6Al-4V structure directly produced by the SEBM process as scaffolds for bone formation. SEBM-processed titanium implants were placed into defects in the frontal skull of 15 domestic pigs. To evaluate the direct contact between bone and implant surfaces and to assess the ingrowth of osseous tissue into the porous structure, microradiographs and histomorphometric analyses were performed 14, 30, and 60 days after surgery. Bone ingrowth increased significantly during the period of this study. After 14 days the most outer regions of the implants were already filled with newly formed bone tissue (around 14%). After 30 days the bone volume inside the implants reached almost 30% and after 60 days abundant bone formation inside the implants attained 46%. During the study only scarce bone-implant contact was found around all implants, which did not exceed 9% around compact specimens and 6% around porous specimens after 60 days. This work demonstrates that highly porous titanium implants with excellent interconnectivity manufactured using the SEBM method are suitable scaffolds for bone ingrowth. This technique is a good candidate for orthopedic and maxillofacial applications.

Maintenance of a bone collagen phenotype by osteoblast-like cells in 3D periodic porous titanium (Ti-6Al-4 V) structures fabricated by selective electron beam melting

Abstract Regular 3D periodic porous Ti-6Al-4 V structures were fabricated by the selective electron beam melting method (EBM) over a range of relative densities (0.17–0.40) and pore sizes (500–1500 µm). Structures were seeded with human osteoblast-like cells (SAOS-2) and cultured for four weeks. Cells multiplied within these structures and extracellular matrix collagen content increased. Type I and type V collagens typically synthesized by osteoblasts were deposited in the newly formed matrix with time in culture. High magnification scanning electron microscopy revealed cells attached to surfaces on the interior of the structures with an increasingly fibrous matrix. The in-vitro results demonstrate that the novel EBM-processed porous structures, designed to address the effect of stress-shielding, are conducive to osteoblast attachment, proliferation and deposition of a collagenous matrix characteristic of bone.

Biomechanical behavior of bone scaffolds made of additive manufactured tricalciumphosphate and titanium alloy under different loading conditions.

Purpose The repair of large segmental bone defects caused by fracture, tumor or infection remains challenging in orthopedic surgery. The capability of two different bone scaffold materials, sintered tricalciumphosphate and a titanium alloy (Ti6Al4V), were determined by mechanical and biomechanical testing. Methods All scaffolds were fabricated by means of additive manufacturing techniques with identical design and controlled pore geometry. Small-sized sintered TCP scaffolds (10 mm diameter, 21 mm length) were fabricated as dense and open-porous samples and tested in an axial loading procedure. Material properties for titanium alloy were determined by using both tensile (dense) and compressive test samples (open-porous). Furthermore, large-sized open-porous TCP and titanium alloy scaffolds (30 mm in height and diameter, 700 μm pore size) were tested in a biomechanical setup simulating a large segmental bone defect using a composite femur stabilized with an osteosynthesis plate. Static physiologic loads (1.9 kN) were applied within these tests. Results Ultimate compressive strength of the TCP samples was 11.2 ± 0.7 MPa and 2.2 ± 0.3 MPa, respectively, for the dense and the open-porous samples. Tensile strength and ultimate compressive strength was 909.8 ± 4.9 MPa and 183.3 ± 3.7 MPa, respectively, for the dense and the open-porous titanium alloy samples. Furthermore, the biomechanical results showed good mechanical stability for the titanium alloy scaffolds. TCP scaffolds failed at 30% of the maximum load. Conclusions Based on recent data, the 3d printed TCP scaffolds tested cannot currently be recommended for high load-bearing situations. Scaffolds made of titanium could be optimized by adapting the biomechanical requirements.