Strong flux pinning enhancement in YBa2Cu3O7−x films by embedded BaZrO3 and BaTiO3 nanoparticles

YBa2Cu3O7−x (YBCO) films with embedded BaZrO3 and BaTiO3 nanoparticles were fabricated by metalorganic deposition using trifluoroacetates (TFA-MOD). Both X-ray diffraction and transmission electron microscopy revealed that these BaZrO3 and BaTiO3 nanoparticles had random orientations and were distributed stochastically in the YBCO matrix. The unique combined microstructure enhances the critical current density (Jc) of the BaZrO3/BaTiO3 doped-YBCO films, while keeping the critical transition temperature (Tc) close to that in the pure YBCO films. These results indicate that BaZrO3 and BaTiO3 nanoparticles provide strong flux pinning in YBCO films.

Effects of thickness on superconducting properties and structures of Y2O3/BZO-doped MOD-YBCO films

We report the thickness dependence of critical current density (Jc) in YBa2Cu3O7−x (YBCO) films with BaZrO3 (BZO) and Y2O3 additions grown on single crystal LaAlO3 substrates by metalorganic deposition using trifluoroacetates (TFA-MOD). Comparing with pure YBCO films, the Jc of BZO/Y2O3-doped YBCO films was significantly enhanced. It was also found that with the increase of the thickness of YBCO film from 0.25 μm to 1.5 μm, the Ic of BZO/Y2O3-doped YBCO film increased from 130 A/cm to 250 A/cm and yet Jc of YBCO film decreased from 6.5 MA/cm2 to 2.5 M A/cm2. The thick BZO/Y2O3-doped MOD-YBCO film showed lower Jc, which is mainly attributed to the formation of a-axis grains and pores.