Ricardo Rodrigues Vaz

Bond strength and interfacial micromorphology of etch-and-rinse and self-adhesive resin cements to dentin.

PURPOSE To evaluate the microtensile bond strength and interfacial micromorphology of indirect composite restorations to dentin using three commercial resin cements after 24 hours and 30 days of water storage. MATERIALS AND METHODS The medium dentin of third human molars was exposed (N = 30, n = 10 per group). Three commercial resin cements were used to cement indirect resin composite restorations to dentin: the auto-cured C&B Cement/All Bond 2, the dual-cured RelyX ARC/Adper Single Bond 2, and the self-adhesive dual-cured RelyX Unicem. Teeth were sectioned after water storage at 37°C (24 hours and 30 days) to obtain beams with a bonded area of 0.8 mm(2) . The specimens were tested in a universal testing machine at a 0.5 mm/min crosshead speed. Scanning electron microscopic fractographic and interfacial micromorphology analyses were performed. Data were analyzed using two-way ANOVA and Tukeys test (α= 0.05). RESULTS Mean bond strength (MPa) after 24 hours: C&B Cement 19.5 ± 3.8, RelyX ARC 40.8 ± 9.4, RelyX Unicem 31.3 ± 7.4; after 30 days: C&B Cement 24.5 ± 5.1, RelyX ARC 44.2 ± 8.5, RelyX Unicem 28.3 ± 7.1. The mean bond strengths of both dual-cure cements were significantly higher than that obtained with C&B Cement after 24 hours. A significant increase in the bond strength of C&B Cement was verified after 30 days, reaching values statistically equivalent to those produced by RelyX Unicem and RelyX ARC. The self-adhesive cement preserved the same level of bond strength after 30 days. Fractographic analysis revealed a prevalence of cohesive fractures in the hybrid layer for C&B Cement, mixed (cohesive in the cement, hybrid layer, and adhesive) for RelyX ARC, and cohesive in the cement for RelyX Unicem. No distinguishable hybrid layer or resin tags were observed in the interaction of RelyX Unicem with dentin. CONCLUSIONS The particular interaction of each cement with dentin results in specific bond strength and failure patterns that varied among groups in both evaluation times. Even though the self-adhesive cement tested exhibited no authentic hybrid layer, it was able to promote reliable adhesion with the underlying dentin.

Immunolocalization of HLA-DR and metallothionein on amalgam tattoos

Despite studies concerning toxic reactions related to amalgam components in the literature, few studies have been devoted to evaluate local noxious effects of amalgam tattoos (AT) on biological tissues. In addition, little is known about activation of inflammatory cells by mucosa-implanted amalgam debris. Tissue reaction to AT depends on the particle size. Human leukocyte antigen DR (HLA-DR) is an activation marker of inflammatory cells associated with antigen presentation. Metallothioneins (MT) are proteins involved with metal detoxication, including mercury and silver. The purpose of the present study was to investigate the immunolocalization of HLA-DR and MT in AT with large or powdered particles. Paraffin-embedded AT tissue blocks were sectioned and subjected to immunohistochemistry for HLA-DR and MT localization. The results demonstrated a dense mononuclear inflammatory infiltrate associated with large and powdered debris and positivity for HLA-DR and MT in inflammatory cells. While blood vessel walls and connective fibers impregnated with powdered particles were negative for HLA-DR, they were positive for MT. In addition, wherever epithelial basement membrane impregnation by powdered amalgam particles was observed, a strong positivity for MT was detected. These findings demonstrate that residual elements of AT still have noxious local effects over tissues.