Production of FeCrAlY and CoCrAlY coatings by laser surface fusion and their oxidation behavior

Abstract In this paper the results of a study aimed at coating large areas with FeCrAlY and CoCrAlY alloys by laser surface fusion are described. Metallurgical characteristics and oxidation behavior of the coatings are discussed. The results indicate that fusion of the coating materials was complete and a metallurgical bond was formed between the coatings and the type 304 stainless steel (SS) substrate as a result of laser processing. Some dilution of the coating alloys, in particular the aluminum content, was noticed due to melting of a portion of the substrate. Some small cracks, observed in the CoCrAlY coating, were formed as a result of shrinkage during solidification. Oxidation studies were performed at 1000–1185 °C in air for various times. The coatings, although diluted, showed excellent oxidation resistance and protection, while the type 304 SS substrate deteriorated rapidly. The effect of the thermal and oxidation treatment on the microstructural and chemical stabilities of the coatings are discussed.