Roger J. Guillory

Metallic zinc exhibits optimal biocompatibility for bioabsorbable endovascular stents

Although corrosion resistant bare metal stents are considered generally effective, their permanent presence in a diseased artery is an increasingly recognized limitation due to the potential for long-term complications. We previously reported that metallic zinc exhibited an ideal biocorrosion rate within murine aortas, thus raising the possibility of zinc as a candidate base material for endovascular stenting applications. This study was undertaken to further assess the arterial biocompatibility of metallic zinc. Metallic zinc wires were punctured and advanced into the rat abdominal aorta lumen for up to 6.5months. This study demonstrated that metallic zinc did not provoke responses that often contribute to restenosis. Low cell densities and neointimal tissue thickness, along with tissue regeneration within the corroding implant, point to optimal biocompatibility of corroding zinc. Furthermore, the lack of progression in neointimal tissue thickness over 6.5months or the presence of smooth muscle cells near the zinc implant suggest that the products of zinc corrosion may suppress the activities of inflammatory and smooth muscle cells.

Transition-Metal-Mediated Release of Nitric Oxide (NO) from S-Nitroso-N-acetyl-d-penicillamine (SNAP): Potential Applications for Endogenous Release of NO at the Surface of Stents Via Corrosion Products

Nitric oxide (NO), identified over the last several decades in many physiological processes and pathways as both a beneficial and detrimental signaling molecule, has been the subject of extensive research. Physiologically, NO is transported by a class of donors known as S-nitrosothiols. Both endogenous and synthetic S-nitrosothiols have been reported to release NO during interactions with certain transition metals, primarily Cu(2+) and Fe(2+). Ag(+) and Hg(2+) have also been identified, although these metals are not abundantly present in physiological systems. Here, we evaluate Pt(2+), Fe(2+), Fe(3+), Mg(2+), Zn(2+), Mn(2+), Co(2+), Ni(2+), and Cu(2+) for their ability to generate NO from S-nitroso-N-acetyl-d-penicillamine (SNAP) under physiological pH conditions. Specifically, we report NO generation from RSNOs initiated by three transition metal ions; Co(2+), Ni(2+), and Zn(2+), which have not been previously reported to generate NO. Additionally, preliminary in vivo evidence of zinc wires implanted in the rat arterial wall and circulating blood is presented which demonstrated inhibited thrombus formation after 6 months. One potentially useful application of these metal ions capable of generating NO from RSNOs is their use in the fabrication of biodegradable metallic stents capable of generating NO at the stent-blood interface, thereby reducing stent-related thrombosis and restenosis.

Long-term surveillance of zinc implant in murine artery: Surprisingly steady biocorrosion rate

Metallic zinc implanted into the abdominal aorta of rats out to 6months has been demonstrated to degrade while avoiding responses commonly associated with the restenosis of vascular implants. However, major questions remain regarding whether a zinc implant would ultimately passivate through the production of stable corrosion products or via a cell mediated fibrous encapsulation process that prevents the diffusion of critical reactants and products at the metal surface. Here, we have conducted clinically relevant long term in vivo studies in order to characterize late stage zinc implant biocorrosion behavior and products to address these critical questions. We found that zinc wires implanted in the murine artery exhibit steady corrosion without local toxicity for up to at least 20months post-implantation, despite a steady buildup of passivating corrosion products and intense fibrous encapsulation of the wire. Although fibrous encapsulation was not able to prevent continued implant corrosion, it may be related to the reduced chronic inflammation observed between 10 and 20months post-implantation. X-ray elemental and infrared spectroscopy analyses confirmed zinc oxide, zinc carbonate, and zinc phosphate as the main components of corrosion products surrounding the Zn implant. These products coincide with stable phases concluded from Pourbaix diagrams of a physiological solution and in vitro electrochemical impedance tests. The results support earlier predictions that zinc stents could become successfully bio-integrated into the arterial environment and safely degrade within a time frame of approximately 1-2years. STAEMENT OF SIGNIFICANCE Previous studies have shown zinc to be a promising candidate material for bioresorbable endovascular stenting applications. An outstanding question, however, is whether a zinc implant would ultimately passivate through the production of stable corrosion products or via a cell mediated tissue encapsulation process that prevented the diffusion of critical reactants and products at the metal surface. We found that zinc wires implanted in the murine artery exhibit steady corrosion for up to at least 20months post-implantation. The results confirm earlier predictions that zinc stents could safely degrade within a time frame of approximately 1-2years.

Zn-Li alloy after extrusion and drawing: Structural, mechanical characterization, and biodegradation in abdominal aorta of rat

Zinc shows great promise as a bio-degradable metal. Our early in vivo investigations implanting pure zinc wires into the abdominal aorta of Sprague-Dawley rats revealed that metallic zinc does not promote restenotic responses and may suppress the activities of inflammatory and smooth muscle cells. However, the low tensile strength of zinc remains a major concern. A cast billet of the Zn-Li alloy was produced in a vacuum induction caster under argon atmosphere, followed by a wire drawing process. Two phases of the binary alloy identified by x-ray diffraction include the zinc phase and intermetallic LiZn4 phase. Mechanical testing proved that incorporating 0.1wt% of Li into Zn increased its ultimate tensile strength from 116±13MPa (pure Zn) to 274±61MPa while the ductility was held at 17±7%. Implantation of 10mm Zn-Li wire segments into abdominal aorta of rats revealed an excellent biocompatibility of this material in the arterial environment. The biodegradation rate for Zn-Li was found to be about 0.008mm/yr and 0.045mm/yr at 2 and 12months, respectively.

Evaluation of wrought Zn–Al alloys (1, 3, and 5 wt % Al) through mechanical and in vivo testing for stent applications

Special high grade zinc and wrought zinc-aluminum (Zn-Al) alloys containing up to 5.5 wt % Al were processed, characterized, and implanted in rats in search of a new family of alloys with possible applications as bioabsorbable endovascular stents. These materials retained roll-induced texture with an anisotropic distribution of the second-phase Al precipitates following hot-rolling, and changes in lattice parameters were observed with respect to Al content. Mechanical properties for the alloys fell roughly in line with strength (190-240 MPa yield strength; 220-300 MPa ultimate tensile strength) and elongation (15-30%) benchmarks, and favorable elastic ranges (0.19-0.27%) were observed. Intergranular corrosion was observed during residence of Zn-Al alloys in the murine aorta, suggesting a different corrosion mechanism than that of pure zinc. This mode of failure needs to be avoided for stent applications because the intergranular corrosion caused cracking and fragmentation of the implants, although the composition of corrosion products was roughly identical between non- and Al-containing materials. In spite of differences in corrosion mechanisms, the cross-sectional reduction of metals in murine aorta was nearly identical at 30-40% and 40-50% after 4.5 and 6 months, respectively, for pure Zn and Zn-Al alloys. Histopathological analysis and evaluation of arterial tissue compatibility around Zn-Al alloys failed to identify areas of necrosis, though both chronic and acute inflammatory indications were present.

Fabrication and Short-Term in Vivo Performance of a Natural Elastic Lamina-Polymeric Hybrid Vascular Graft

Although significant advances have been made in the development of artificial vascular grafts, small-diameter grafts still suffer from excessive platelet activation, thrombus formation, smooth muscle cell intimal hyperplasia, and high occurrences of restenosis. Recent discoveries demonstrating the excellent blood-contacting properties of the natural elastic lamina have raised the possibility that an acellular elastic lamina could effectively serve as a patent blood-contacting surface in engineered vascular grafts. However, the elastic lamina alone lacks the requisite mechanical properties to function as a viable vascular graft. Here, we have screened a wide range of biodegradable and biostable medical-grade polymers for their ability to adhere to the outer surface of the elastic lamina and allow cellular repopulation following engraftment in the rat abdominal aorta. We demonstrate a novel method for the fabrication of elastic lamina-polymeric hybrid small-diameter vascular grafts and identify poly(ether urethane) (PEU 1074A) as ideal for this purpose. In vivo results demonstrate graft patency over 21 days, with low thrombus formation, mild inflammation, and the general absence of smooth muscle cell hyperplasia on the grafts luminal surface. The results provide a new direction for developing small-diameter vascular grafts that are mass-producible, shelf-stable, and universally compatible due to a lack of immune response and inhibit the in-graft restenosis response that is common to nonautologous materials.

Novel high-strength, low-alloys Zn-Mg (< 0.1 wt% Mg) and their arterial biodegradation

It is still an open challenge to find a biodegradable metallic material exhibiting sufficient mechanical properties and degradation behavior to serve as an arterial stent. In this study, Zn-Mg alloys of 0.002 (Zn-002Mg), 0.005 (Zn-005Mg) and 0.08wt% Mg (Zn-08Mg) content were cast, extruded and drawn to 0.25mm diameter, and evaluated as potential biodegradable stent materials. Structural analysis confirmed formation of Mg2Zn11 intermetallic in all three alloys with the average grain size decreasing with increasing Mg content. Tensile testing, fractography analysis and micro hardness measurements showed the best integration of strength, ductility and hardness for the Zn-08Mg alloy. Yield strength, tensile strength, and elongation to failure values of >200-300MPa, >300-400MPa, and >30% respectively, were recorded for Zn-08Mg. This metal appears to be the first formulated biodegradable material that satisfies benchmark values desirable for endovascular stenting. Unfortunately, the alloy reveals signs of age hardening and strain rate sensitivity, which need to be addressed before using this metal for stenting. The explants of Zn-08Mg alloy residing in the abdominal aorta of adult male Sprague-Dawley rats for 1.5, 3, 4.5, 6 and 11months demonstrated similar, yet slightly elevated inflammation and neointimal activation for the alloy relative to what was recently reported for pure zinc.

Fibrosis worsens chronic lymphedema in rodent tissues

Secondary lymphedema in humans is a common consequence of lymph node dissection (LND) to treat breast cancer. A peculiar characteristic of the disease is that lifelong swelling often precipitously appears several years after the surgical treatment, often due to an inflammatory stimulus. Although the incidence of secondary lymphedema dramatically increases after radiation therapy, the relationship between fibrotic scarring and the eventual appearance of lymphedema remains unclear. To clarify the role of fibrosis in secondary lymphedema initiation, we chemically increased fibrosis in rodent tissues with bleomycin and assessed the ability of the local lymphatic system to prevent lymphedema, either acutely or in a chronic state induced by inflammation. We found that bleomycin injections exacerbated fibrotic matrix deposition in an acute mouse tail lymphedema model (P < 0.005), reduced wound closure (P < 0.005), and impaired the ability of tail lymphatics to regenerate (P < 0.005) and reduce the swelling (P < 0.05). When fibrosis was worsened with bleomycin after axillary LND in the rat foreleg, the ability of the foreleg lymphatic system to reduce the chronic state swelling induced by stimulated inflammation was severely impaired (P < 0.005). Indocyanine green lymphography in axillary LND-recovered rat forelegs revealed a worsened lymphatic drainage due to inflammation and bleomycin pretreatment. Although inflammation reduced the drainage of dextran fluid tracer from control forelegs (P < 0.05), the reduction in fluid drainage was more severe after axillary LND when fibrosis was first increased (P < 0.005). These findings demonstrate that fibrosis reduces the lymphatic capacity to functionally regenerate and prevent the chronic appearance of lymphedema.

Magnetoelastic galfenol as a stent material for wirelessly controlled degradation rates: MAGNETOELASTIC GALFENOL AS A STENT MATERIAL

The gold standard of care for coronary artery disease, a leading cause of death for in the world, is balloon angioplasty in conjunction with stent deployment. However, implantation injuries and long-term presence of foreign material often promotes significant luminal tissue growth, leading to a narrowing of the artery and severely restricted blood flow. A promising method to mitigate this process is the use of biodegradable metallic stents, but thus far they have either degraded too slowly (iron) or disappeared prematurely (magnesium). The present work investigates the use of a unique type of magnetic material, galfenol (iron-gallium), for postoperative wireless control of stent degradation rates. Due to its magnetoelastic property, galfenol experiences longitudinal micron-level elongations when exposed to applied magnetic fields, allowing generation of a microstirring effect that affect its degradation behavior. In vitro indirect cytotoxicity tests on primary rat aortic smooth muscle cells indicated that galfenol byproducts must be concentrated approximately seven times from collected 60 day degradation medium to cause ∼15% of death from all cells. Surface and cross-sectional characterization of the material indicate that galfenol (Fe80 Ga20 ) degradation rates (∼0.55% per month) are insufficient for stenting applications. While this material may not be ideal for comprising the entire stent, there is potential for use in combination with other materials. Furthermore, the ability to control degradation rates postimplantation opens new possibilities for biodegradable stents; additional magnetoelastic materials should be investigated for use in stenting applications.