Comparison of valence band x-ray photoelectron spectrum between Al-N-codoped and N-doped ZnO films

The valence band structures of Al-N-codoped [ZnO:(Al, N)] and N-doped (ZnO:N) ZnO films were studied by normal and soft x-ray photoelectron spectroscopy. The valence-band maximum of ZnO:(Al, N) shifts up to Fermi energy level by about 300 meV compared with that of ZnO:N. Such a shift can be attributed to the existence of a kind of Al-N in ZnO:(Al, N), as supported by core level XPS spectra and comparison of modified Auger parameters. Al-N increased the relative quantity of Zn-N in ZnO:(Al, N), while N-N decreased that of Zn-N in ZnO:N. (c) 2006 American Institute of Physics.

Aluminium doping induced enhancement of p–d coupling in ZnO

Valence-band type Auger lines in Al doped and undoped ZnO were comparatively studied with the corresponding core level x-ray photoelectron spectrography (XPS) spectra as references. Then the shift trend of energy levels in the valence band was that p and p-s-d states move upwards but e and p-d states downwards with increasing Al concentration. The decreased energy of the Zn 3d state is larger than the increased energy of the 0 2p state, indicating the lowering of total energy. This may indicate that Al doping could induce the enhancement of p-d coupling in ZnO, which originates from stronger Al-O hybridization. The shifts of these states and the mechanism were confirmed by valence band XPS spectra and 0 K-edge x-ray absorption spectrography (XAS) spectra. Finally, some previously reported phenomena are explained based on the Al doping induced enhancement of p-d coupling.

Valence state evolution of C60 deposited on Sm film

Ultraviolet photoemission spectra of C60 deposited on Sm film were measured. The results indicate that C60 and Sm can combine with each other to form fulleride in the interface at room temperature. The bonding is mainly ionic with some covalent contribution. Both the lowest unoccupied molecular orbital (LUMO) and the LUMO+1 orbital of C60 are occupied at coverages less than about one monolayer. As for the second overlayer, only the LUMO orbital is occupied. The first and second C60 overlayers are metallic and semiconducting, respectively.