S. Ummartyotin

Deposition of PEDOT: PSS nanoparticles as a conductive microlayer anode in OLEDs device by desktop inkjet printer

A simple microfabrication technique for delivering macromolecules and patterning microelectrode arrays using desktop inkjet printer was described. Aqueous solution of nanoparticle of poly (3,4-ethylenedioxythiophene) (PEDOT) doped with polystyrene sulfonic acid (PSS) was prepared while its particle size, the surface tension, and the viscosity of the solution were adjusted to be suitable for deposition on a flexible cellulose nanocomposite substrate via inkjet printer. The statistical average of PEDOT: PSS particle size of 100nm was observed. The microthickness, surface morphology, and electrical conductivity of the printed substrate were then characterized by profilometer, atomic force microscope (AFM), and four-point probe electrical measurement, respectively. The inkjet deposition of PEDOT: PSS was successfully carried out, whilst retained its transparency feature. Highly smooth surface (roughness ∼23-44 nm) was achieved.