Sachin B. Kulkarni

High-performance supercapacitor electrode based on a polyaniline nanofibers/3D graphene framework as an efficient charge transporter

The current paper describes chemically grown polyaniline (PANI) nanofibers on porous three dimensional graphene (PANI/3D graphene) as a supercapacitor electrode material with enhanced electrochemical performance. The chemical and structural properties of the electrode are characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy with confirmation of a semi-crystalline nature. The homogeneous growth of PANI on the 3D graphene network is visualized by field emission scanning electron microscopy (FESEM) and shows a nanofibers-based morphology. The maximum specific capacitance of the PANI/3D graphene electrode is found to be ∼1024 F g−1 in 1 M H2SO4 within the potential window of −150 to 800 mV vs. Ag/AgCl at 10 mV s−1 scan rate (∼1002 F g−1 at 1 mA cm−2 discharge current density). The high surface area offered by the conducting, porous 3D graphene framework stimulates effective utilization of the deposited PANI and improves electrochemical charge transport and storage. This signifies that the 3D graphene framework is a proficient contender for high-performance capacitor electrodes in energy storage applications.

Enhanced Supercapacitive Performance of Chemically Grown Cobalt–Nickel Hydroxides on Three-Dimensional Graphene Foam Electrodes

Chemical growth of mixed cobalt-nickel hydroxides (CoxNi1-x(OH)2), decorated on graphene foam (GF) with desirable three-dimensional (3D) interconnected porous structure as electrode and its potential energy storage application is discussed. The nanostructured CoxNi1-x(OH)2 films with different Ni:Co (x) compositions on GF are prepared by using the chemical bath deposition (CBD) method. The structural studies (X-ray diffraction and X-ray photoelectron spectroscopy) of electrodes confirm crystalline nature of CoxNi1-x(OH)2/GF and crystal structure consists of Ni(OH)2 and Co(OH)2. The morphological properties reveal that nanorods of Co(OH)2 reduce in size with increases in nickel content and are converted into Ni(OH)2 nanoparticles. The electrochemical performance reveals that the Co0.66Ni0.33(OH)2/GF electrode has maximum specific capacitance of ∼1847 F g(-1) in 1 M KOH within a potential window 0 to 0.5 V vs Ag/AgCl at a discharge current density of 5 A g(-1). The superior pseudoelectrochemical properties of cobalt and nickel are combined and synergistically reinforced with high surface area offered by a conducting, porous 3D graphene framework, which stimulates effective utilization of redox characteristics and communally improves electrochemical performance with charge transport and storage.

Controlled electrochemical growth of Co(OH)2 flakes on 3D multilayered graphene foam for high performance supercapacitors

The present research describes successful enchase of Co(OH)2 microflakes by the potentiodynamic mode of electro-deposition (PED) on porous, light weight, conducting 3D multilayered graphene foam (MGF) and their synergistic effect on improving the supercapacitive performance. Structural and morphological analyses reveal uniform growth of Co(OH)2 microflakes with an average flake width of ∼30 nm on the MGF surface. Moreover, electrochemical capacitive measurements of the Co(OH)2/MGF electrode exhibit a high specific capacitance of ∼1030 F g−1 with ∼37 W h kg−1 energy and ∼18 kW kg−1 power density at 9.09 A g−1 current density. The superior pseudoelectrochemical properties of cobalt hydroxide are synergistically decorated with high surface area offered by a conducting, porous 3D graphene framework, which stimulates the effective utilization of redox characteristics and mutually improves electrochemical capacitive performance with charge transport and storage. This work evokes scalable electrochemical synthesis with the enhanced supercapacitive performance of the Co(OH)2/MGF electrode in energy storage devices.

Post-heating effects on the physical and electrochemical capacitive properties of reduced graphene oxide paper

We report combined electrochemical double-layer capacitance (EDLC) and pseudocapacitance in reduced graphene oxide (rGO) thick film like paper due to annealing temperature variations. The influence of annealing temperature (from room temperature (RT) to 1000 °C) on the structural, morphological, electrical, and electrochemical properties of rGO paper was evaluated. Upon increasing the annealing temperature, shifting of the dominant (002) X-ray diffraction (XRD) peak to a higher degree, volume expansion, and red-shifting of the G band in Raman spectra were observed. High-resolution transmission electron microscopy (HRTEM) images showed a reduction in the interlayer distance in rGO sheets from 0.369 to 0.349 nm as the annealing temperature increased from RT to 1000 °C; these results were congruent with the XRD results. According to X-ray photoelectron spectroscopy (XPS), the presence of hydroxyl, carboxyl, and other oxygen-containing groups decreased in samples annealed at higher temperatures. The attached functional groups, the electrical conductivity, and the supercapacitance of rGO papers were found to be mutually interrelated and could be tuned by varying the annealing temperature. The rGO paper annealed at 200 °C in a 1 M H2SO4 electrolyte at a scan rate of 50 mV s−1 exhibited a maximum specific capacitance of 198 F g−1.