Binary Effect of Fly Ash and Palm Oil Fuel Ash on Heat of Hydration Aerated Concrete

The binary effect of pulverized fuel ash (PFA) and palm oil fuel ash (POFA) on heat of hydration of aerated concrete was studied. Three aerated concrete mixes were prepared, namely, concrete containing 100% ordinary Portland cement (control sample or Type I), binary concrete made from 50% POFA (Type II), and ternary concrete containing 30% POFA and 20% PFA (Type III). It is found that the temperature increases due to heat of hydration through all the concrete specimens especially in the control sample. However, the total temperature rises caused by the heat of hydration through both of the new binary and ternary concrete were significantly lower than the control sample. The obtained results reveal that the replacement of Portland cement with binary and ternary materials is beneficial, particularly for mass concrete where thermal cracking due to extreme heat rise is of great concern.

Strength and Porosity of Cement Mortar Blended with Metakaolin

An experimental investigation was carried out to assess the effect of metakaolin (MK) on the compressive strength, flexural strength and porosity of cement mortar. The cement was partially substituted with MK at 0-30% replacement levels. The results show that the strengths and porosity of mortar containing up to 20% were superior to that of control (0% MK). The Balshin equation fits the experimental results of compressive strength and porosity of the specimens containing MK and there is a strong quantitative relationship between compressive strength and porosity of the specimens.

Properties of binary and ternary blended cement mortars containing palm oil fuel ash and metakaolin

Abstract This paper has investigated the properties of mortars made from binary and ternary blends of metakaolin (MK), palm oil fuel ash (POFA), and ordinary Portland cement (OPC). A total of 17 different mortar mixtures were produced. The OPC in the mixtures was partially replaced by MK, POFA, or a combination of MK and POFA at different replacement levels of (0–30%) by weight of the binder. At the fresh state, the flow (workability) of mortar mixtures was determined, while at the hardened state, the compressive strength and porosity at the ages of 7, 28, and 90 days were evaluated. The results showed that the flow of mortar is boosted with the combined use of MK and POFA compared to when MK is separately used. Besides, improvement in low early compressive strength development and reduction in high porosity from use of POFA occurred with the addition of up to 10% MK content. Therefore, the combination of POFA and MK could be used as a supplementary cementitious material to produce cement-based material of higher quality than OPC.