Effects of Cr and Fe co-doping on structural, optical, electrical and magnetic properties of titanium dioxide (TiO2)

Abstract A series of Ti0.9Fe0.1-xCrxO2 (where x = 0.0, 0.02, 0.04, 0.6, 0.08, 0.10) was synthesized using the powder metallurgy route. The structural, morphological, magnetic, optical and electrical properties were investigated by X-ray diffractometry (XRD), Raman spectroscopy, scanning electron microscopy (SEM), vibrating sample magnetometry (VSM), UV-Vis spectroscopy and four probe technique, respectively. The rutile phase was confirmed by XRD analysis which was also verified by Raman spectroscopy. It was observed that the grain size increased as the concentration of Cr increased. M-H loops extracted from VSM analysis revealed anti-ferromagnetic, weak ferromagnetic and paramagnetic behaviors at room temperature. The band gap energy and resistivity measurements exhibited the semiconducting nature of Ti0.9Fe0.1-xCrxO2 based diluted magnetic semiconductors.

Investigation of Structural, Magnetic, and Optical Properties of ZnO Codoped with Co and Cd

Co and Cd have been codoped in ZnO using a simple solid state reaction technique to synthesize dilute magnetic oxide semiconductors of composition Zn0.9Co0.1−xCdxO ( with an increment of 0.02). Hexagonal wurtzite structure has been obtained for samples up to , using X-ray diffractometry. However, at and 0.1, secondary peak of CdO is observed. Raman spectra of the samples have been obtained in 200–800 cm−1 range. UV-VIS spectrophotometer is used to study the optical properties, which shows that band gap energy decreases with the increase in Cd concentration. A weak ferromagnetic behavior was evident which decreased further by adding Cd in the series. Room temperature resistivity measurements performed using four-point probe technique showed that their values lie in the semiconductor range. Structural morphology of the samples has been investigated by a scanning electron microscope and grain size has been determined. Raman spectra and Fourier transform infrared spectroscopy revealed the successful incorporation of Co and Cd ions into the host ZnO lattice.