Seok Hong Min

Effect of C Content on the Microstructure and Physical Properties of Fe-36Ni Invar Alloy

Thermodynamic equilibrium of Fe-36Ni-base Invar alloy containing C contents from 0.25 to 0.38 weight per cent during solidification has been investigated in this study. From the thermodynamic simulation using ThermoCalc®, it has been revealed that equilibrium phases which can be formed are two kinds of MC-type precipitates, i.e. (Nb, Mo, V)C and MoC, and M2C carbides. The MoC carbide was expected to be formed at relatively lower temperature below 770oC. Microstructure observation revealed the coarse precipitates in the as-cast ingots, which was Mo-rich non-equilibrium phase and could be resolved by the successive heat treatment. With increasing C contents from 0.25 to 0.38 wt.%, tensile strength of Invar alloy increased from 950 to 1100MPa after hot rolling and thermal expansion coefficient showed a trivial increase. Hot-rolled Invar alloy was successfully drawn at room temperature from 6 to 4 mm in diameter, which dramatically decreased thermal expansion coefficient.

Orientation Dependence of Flow Behavior of Mg Single Crystal

Single crystals of pure magnesium were fabricated in this study by employing the modified Bridgman method. To determine the exact orientation of crystals, electron back scattered diffraction (EBSD) method was employed in this study. Dimensions of single crystals were 10 mm in diameter and 120 mm in length. Single crystals with near basal, pyramidal, and near prismatic orientations were obtained, on which hardness and compression tests were conducted. It has been revealed that hardness and the strength strongly depended on the orientation. While the hardness of pyramidal orientation was highest and that of near prismatic orientation was lowest, the compressive strength along near prismatic orientation appeared to be highest and that along prismatic orientation was lowest.

Recrystallization Behavior of Aluminum Thin Foils with Various Purity

Recrystallization kinetics of aluminum with various purities from 99.5 to 99.999(5N) has been investigated in this study. Aluminum plates of 10 mm thickness with various purities were solution-treated at 400oC for 24 hrs and then rolled into sheets of 50 μm thickness at room temperature. Cold rolling was conducted on samples with various purities from 99.9 to 99.999 including commercial AA 1050 Al alloy and high purity through about 20 passes to obtain thin foils of 50 μm thickness. Accumulative rolling was employed when sample thickness reached at 1 mm and thin foils were successfully obtained for all samples. Hardness was measured just after cold rolling at room temperature as a function of time up to 1hr to elucidated recrystallization behavior. For aluminum with 99.999% purity, recrystallization occurred after 200 s and finished at 360 s. Recrystallization kinetics of aluminum at high temperatures from 100 to 350oC were investigated by measure hardness after annealing thin foils for various time intervals ranging from 1 s to 24 hrs. For high purity sample with 99.999% purity, recrystallization finished just after 1 s even at the relatively low temperature of 100oC, while recrystallization of commercial AA 1050 (2N) alloy finished after 360 s at 350oC.

Effect of Boron Addition on Microstructure and Mechanical Properties of AZ84 Mg Alloy

Effect of B addition on the microstructure and mechanical properties of AZ84 Mg alloy was investigated in this study. Through calculation of phase equilibria of AZ84 Mg alloy, carried out by using FactSage® and FTLite database, solution treatment temperature was decided as temperature of 330oC, where supersaturated solid solution can be obtained. Solid solution treatment of AZ84 Mg alloy was successfully conducted at 330oC and supersaturated microstructure with all almost all phases resolved into matrix was obtained. After solution treatment, hot rolling was successfully conducted by reduction of 60%. Compression and tension tests were carried out at room temperature on the samples in as-cast, solution treated, hot-rolled and subsequently recrystallized states. After solid solution treatment, each alloy was soaked at temperatures of 180 and 200oC for time intervals from 1 min to 48 hrs and hardness of each condition was measured by micro-Vickers method. Peak aging conditions were deduced as at the temperature of 200 oC for 10 hrs for ZA84 Mg alloy. By addition of boron, aging kinetics was expedited and strength was enhanced.