Selective Oxidation of CO in Excess H2 over Ru/Al2O3 Catalysts Modified with Metal Oxide

Abstract The Ru/Al2O3 catalysts modified with metal oxide (K2OandLa2O3) were prepared via incipient wetness impregnation method from RuCl3·nH2O mixed with nitrate loading on Al2O3 support. The activity of catalysts was evaluated under simulative conditions for the preferential oxidation of CO (CO-PROX) from the hydrogen-rich gas streams produced by reforming gas, and the performances of catalysts were investigated by XRD and TPR. The results showed that the activity temperature of the modified catalysts Ru-K2O/Al2O3 and Ru-La2O3/Al2O3 were lowered approximately 30 °C compared with pure Ru/Al2O3, and the activity temperature range was widened. The conversion of CO on Ru-K2O/Al2O3 and Ru-La2O3/Al2O3 was above 99% at 140–160 °C, suitable to remove CO in a hydrogen-rich gas and the selectivity of Ru-La2O3/Al2O3 was higher than that of Ru-K2O/Al2O3 in the active temperature range. Slight methanation reaction was detected at 220 °C and above.

Carbon nanotubes supported Pt-Ru-Ni as methanol electro-oxidation catalyst for direct methanol fuel cells

Abstract Carbon nanotubes (CNTs) supported Pt-Ru and Pt-Ru-Ni catalysts were prepared by chemical reduction of metal precursors with sodium borohydride at room temperature. The crystallographic properties and composition of the catalysts were characterized by X-ray diffraction (XR, D) and energy dispersive X-ray (EDX) analysis, and the catalytic activity and stability for methanol electro-oxidation were measured by electrochemical impedance spectroscopy (EIS), linear sweep voltammetries (LSV), and chronoamperometry (CA). The results show that the catalysts exhibit face-centered cubic (fee) structure. The particle size of Pt-R.u-Ni/CNTs catalyst is about 4.8 nm. The catalytic activity and stability of the Pt-Ru-Ni/CNTs catalyst are higher than those of Pt-Ru/CNTs catalyst.

Carbon nanotubes-Nafion composites as Pt-Ru catalyst support for methanol electro-oxidation in acid media

Carbon nanotubes-Nafion (CNTs-Nafion) composites were prepared by impregnated CNTs with Nafion in ethanol solution and characterized by FT-IR. Pt-Ru catalysts supported on CNTs-Nafion composites were synthesized by microwave-assisted polyol process. The physical and electrochemical properties of the catalysts were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), CO stripping voltammetry, cyclic voltammetry (CV) and chronoamperometry (CA). The results showed that the Nafion incorporation in CNTs-Nafion composites did not significantly alter the oxygen-containing groups on the CNTs surface. The Pt-Ru catalyst supported on CNTs-Nafion composites with 2 wt% Nafion showed good dispersion and the best CO oxidation and methanol electro-oxidation activities.

Effect of pretreatment methods on the performance of Cu-Zr-Ce-O catalyst for CO selective oxidation

Abstract The Cu-Zr-Ce-O catalysts prepared using the coprecipitation method exhibited better catalytic performance for CO selective oxidation. The Cu-Zr-Ce-O catalysts pretreated with different methods were studied by CO-TPR and XPS techniques. The results showed that the Cu-Zr-Ce-O catalyst pretreated with oxygen exhibited the best catalytic performance and had the widest operating temperature window, with CO conversion above 99% from 160 to 200° C. The O 2 pretreatment caused an enrichment of the oxygen storaged on the Cu active species and promoted the conversion of adsorbed oxygen into surface lattice oxygen. It also improved the amount of Cu + /Cu 2+ ionic pair, and then facilitated the formation of CuO active species on the catalyst for selective CO oxidation.

In Situ Carbon Coated LiNi0.5Mn1.5O4 Cathode Material Prepared by Prepolymer of Melamine Formaldehyde Resin Assisted Method

Carbon coated spinel LiNi0.5Mn1.5O4 were prepared by spray-drying using prepolymer of melamine formaldehyde resin (PMF) as carbon source of carbon coating layer. The PMF carbon coated LiNi0.5Mn1.5O4 was characterized by XRD, SEM, and other electrochemical measurements. The as-prepared lithium nickel manganese oxide has the cubic face-centered spinel structure with a space group of Fd3m. It showed good electrochemical performance as a cathode material for lithium ion battery. After 100 discharge and charge cycles at 0.5 C rate, the specific discharge capacity of carbon coated LiNi0.5Mn1.5O4 was 130 mAh·g−1, and the corresponding capacity retention was 98.8%. The 100th cycle specific discharge capacity at 10 C rate of carbon coated LiNi0.5Mn1.5O4 was 105.4 mAh·g−1, and even the corresponding capacity retention was 95.2%.

Study on the Catalytic Performance of CuO-CeO2 Catalysts Doped with Transition Metal Oxides for Selective CO Oxidation

A series of CuO-CeO2 catalysts doped with transition metal oxides were prepared by co-precipitation method for selective CO oxidation and the effects of the additives on the catalytic performance were examined by H2-TPR, in-situ DRIFTS techniques. The results showed that the main CO adsorption site on CuO-CeO2 series catalysts was Cu+ species. The catalytic activity at lower temperatures was related to the CO desorption. The doping of ZnO improved the catalytic activity evidently and the CO conversion and selectivity of Cu1Zn1Ce9Od could reach 99.9% and 76.4% at 160°C, respectively. ZnO not only stabilized the reduced Cu+ species, but also increased the capacity of CO adsorption.