Large-Scale Synthesis and Microwave Absorption Enhancement of Actinomorphic Tubular ZnO/CoFe2O4 Nanocomposites

Actinomorphic tubular ZnO/CoFe(2)O(4) nanocomposites were fabricated in large scale via a simple solution method at low temperature. The phase structures, morphologies, particle size, shell thickness, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), energy dispersive X-ray spectroscopy (EDS), and transmission electron microscopy (TEM). The as-synthesized nanocomposites were uniformly dispersed into the phenolic resin then the mixture was pasted on metal plate with the area of 200 mm x 200 mm as the microwave absorption test plate. The test of microwave absorption was carried out by the radar-absorbing materials (RAM) reflectivity far field radar cross-section (RCS) method. The range of microwave absorption is from 2 to 18 Hz and the best microwave absorption reach to 28.2 dB at 8.5 Hz. The results indicate that the composites are of excellence with respect to microwave absorption.

Structural, electrical and optical properties of yttrium-doped ZnO thin films prepared by sol–gel method

Yttrium-doped ZnO thin films were deposited on silica glass substrates by the sol–gel method. The structural, electrical and optical properties of yttrium-doped ZnO thin films were investigated systematically and in detail. All the thin films have a preferred (0 0 2) orientation. When compared with the electrical resistivity values of films without annealing treatment, the values of films annealed in the reducing atmosphere were decreased by about three orders of magnitude. The lowest electrical resistivity value was 6.75 × 10−3 Ω cm, which was obtained in the 0.5 at% yttrium-doped ZnO thin film annealed in nitrogen with 5% hydrogen at 500 °C. In room-temperature photoluminescence (PL) spectra, two PL emission peaks are found in the pure ZnO thin film; one is the near-band-edge (NBE) emission at 3.22 eV and the other is a green emission at about 2.38 eV. Nevertheless, the green emission is not found in the PL of the yttrium-doped ZnO thin films. The low-temperature PL spectrum of the undoped ZnO thin film at 83 K is split into well-resolved free and bound excition emission peaks in the ultraviolet region, but the NBE emission of the 5 at% yttrium-doped ZnO thin film at 83 K has only one broad emission peak.