Nanostructure of and structural defects in a Mo2BC hard coating investigated by transmission electron microscopy and atom probe tomography

In this work, the nanostructure of a Mo2BC hard coating was determined by several transmission electron microscopy methods and correlated with the mechanical properties. The coating was deposited on a Si (100) wafer by bipolar pulsed direct current magnetron sputtering from a Mo2BC compound target in Ar at a substrate temperature of 630 °C. Transmission electron microscopy investigations revealed structural features at various length scales: bundles (30 nm to networks of several micrometers) consisting of columnar grains (∼10 nm in diameter), grain boundary regions with a less ordered atomic arrangement, and defects including disordered clusters (∼1.5 nm in diameter) as well as stacking faults within the grains. The most prominent defect with a volume fraction of ∼0.5% is the disordered clusters, which were investigated in detail by electron energy loss spectroscopy and atom probe tomography. The results provide conclusive evidence that Ar is incorporated into the Mo2BC film as disordered Ar-rich Mo-B-C c...