Mechanistic studies of atmospheric pitting corrosion of stainless steel for ILW containers

Abstract Atmospheric pitting corrosion of stainless steel was examined with synchrotron X-ray microtomography, laboratory based tests and electrochemical measurements in order to provide a mechanistic basis for the development of corrosion prediction models. It was found that the morphology of corrosion pits was affected by the presence of residual ferrite, and some pits showed dense covers that may affect pit stability. Fluctuations in relative humidity may lead to partial or complete repassivation of pits, sometimes leading to the formation of new pits. Electrochemical measurements in artificial pits containing concentrated salt solutions show a strong dependence of the diffusion limited current density on chloride concentration.

Effect of Microstructure on the Morphology of Atmospheric Corrosion Pits in 304L Stainless Steel

Atmospheric corrosion of stainless steel is of concern for intermediate level nuclear waste (ILW) containers. The effect of microstructure on the morphology of atmospheric corrosion pits in Type 30...

In Situ Synchrotron X-Ray Diffraction Characterization of Corrosion Products of a Ti-Based Metallic Glass for Implant Applications

Ti-based bulk metallic glasses are under consideration for implants due to their high yield strength and biocompatibility. In this work, in situ synchrotron X-ray diffraction (XRD) is used to investigate the corrosion products formed from corrosion of Ti40 Zr10 Cu34 Pd14 Sn2 bulk metallic glass in artificial corrosion pits in physiological saline (NaCl). It is found that Pd nanoparticles form in the interior of the pits during electrochemical dissolution. At a low pit growth potential, the change in lattice parameter of the Pd nanoparticles is consistent with the formation of palladium hydride. In addition, a salt layer very close to the dissolving interface is found to contain CuCl, PdCl2 , ZrOCl2 ∙8H2 O, Cu, Cu2 O, and several unidentified phases. The formation of Pd nanoparticles (16 ± 10 nm at 0.7 V vs Ag/AgCl) containing small amounts of the other alloying elements is confirmed by transmission electron microscopy. The addition of albumin and/or H2 O2 does not significantly influence the nature of the corrosion products. When considering the biological compatibility of the alloy, the biological reactivity of the corrosion products identified should be explored.