Surachet Phadungdhitidhada

Surface Modification of Porous Photoelectrode Using Etching Process for Efficiency Enhancement of ZnO Dye-Sensitized Solar Cells

Surface modification of porous ZnO photoelectrode using one- and two-step etching process is investigated for enhancing power conversion efficiency of ZnO dye-sensitized solar cells. ZnO films are modified by the diluted NH4OH solutions for one-step etching process and used as photoelectrode of dye-sensitized solar cells. Rough porous films are observed after one-step etching process. The fabricated cells based on the optimized one-step etched films show a significant increase in short-circuit current density. The short-circuit current density is directly changed with amount of dye adsorption, which is related to specific surface area. The etched films exhibit higher specific surface area over two times than nonetched films. Thus, the large specific surface area is the key success for increasing amount of dye adsorption. Internal electrochemical property of fabricated cells is also improved, indicating that chemical surface of ZnO films is modified in the same time. The DSSCs fabricated on two-step etched films with NH4OH and mixed acid HCl : HNO3 show the maximum power conversion efficiency of 2.26%. Moreover, fill factor is also increased due to better redox process because of the formation of fine porous structure during the etching process. Therefore, these results implied that the roles of etching processes are improving specific surface area and fine porous formation which can provide better dye adsorption and redox process for dye-sensitized solar cell application.

Synthesis and Characterization of MgO by Microwave-Assisted Thermal Oxidation for Dye-Sensitized Solar Cells

Magnesium oxide (MgO) nanostructures were synthesized by microwave-assisted thermal oxidation at various amount of activated carbon additive. The MgO nanostructures were characterized by scanning electron microscopy (SEM), Transmission electron microscopy (TEM), X-ray diffractrometry (XRD) and UV-Visible spectroscopy, respectivly. It was observed that, the obtained MgO have nanocube shape. The MgO nanostructures were applied as a blocking layer in ZnO dye-sensitized solar cells (DSSC). The photovoltage, photocurrent, and power conversion efficiency characteristics of DSSCs were measured under illumination of simulated sunlight obtained from a solar simulator with the radiant power of 100 mW/cm2. The DSSCs with MgO layer exhibited higher current density, open circuit voltage and photoconversion efficiency than those without MgO layer The optimum power conversion efficiency (PCE) was 2.49 % with short circuit current (Jsc) of 6.61 mA/cm2, the open circuit voltage (Voc) of 0.66 V and the fill factor (FF) of 0.59, respectively.