New insight into melting and crystallization behavior in semicrystalline poly(ethylene terephthalate)

After isothermal crystallization, poly(ethylene terephthalate) (PET) showed double endothermic behavior in the differential scanning calorimetry (DSC) heating scan. During the heating scans of semicrystalline PET, a metastable melt which comes from melting thinner lamellar crystal populations formed between the low and the upper endothermic temperatures. The metastable melt can recrystallize immediately just above the low melting temperature and form thicker lamellae than the original ones. The thickness and perfection depends on the crystallization time and crystallization temperature. The crystallization kinetics of this metastable melt can be determined by means of DSC. The kinetics analysis showed that the isothermal crystallization of the metastable PET melt proceeds with an Avrami exponent of n = 1.0 similar to 1.2, probably reflecting one-dimensional or irregular line growth of the crystal occurring between the existing main lamellae with heterogeneous nucleation. This is in agreement with the hypothesis that the melting peaks are associated with two distinct crystal populations with different thicknesses

Crystallization kinetics of poly(ether ether ketone) (PEEK) from its metastable melt

After isothermal crystallization of the amorphous poly(ether ether ketone), double endothermic behaviour can be found through differential scanning calorimetry experiments. During the heating scan of semicrystalline PEEK, a metastable melt, which comes from the melt of the thinner lamellar crystal populations, can be obtained between these two endotherms. The metastable melt can recrystallize immediately just above the lower melting temperature and form slightly thicker lamellae than the original ones. The thickness and the perfection depend upon the crystallization time and the crystallization temperature. By comparing the TEM morphological observations of the samples before and after partial melting, it can be shown that lamellar crystals, having different thermodynamic stability, form during isothermal crystallization. After partial melting, only the type of lamellar crystal exhibiting the higher thermodynamic stability remains. Wide angle X-ray diffraction measurements shows a slightly change in the crystallinity of the samples before and after the partial melting. Small angle X-ray scattering results exhibit a change in the long period of the lamellar crystals before and after the partial melting process. The crystallization kinetics of the metastable melt can be determined by means of differential scanning calorimetry. The kinetic analysis showed that the isothermal crystallization of the metastable PEEK melt proceeds with an Avrami exponent of n = 1.0 similar to 1.4, reflecting that probably one-dimensional or an irregular line growth of the crystal occurred between the existing main lamellae with heterogeneous nucleation

Spatially-confined crystallization of poly(vinylidene fluoride)

Nanometre-sized poly(vinylidene fluoride) (PVDF) particle domains in a confined space were obtained by blending PVDF with excess poly(methyl methacrylate) (PMMA). When these particles were small enough they showed beta -form structure, which was different from the structure of bigger particles or PVDF bulk. However, the beta -form was thermodynamically metastable because it could eventually be transformed to a more stable phase by annealing at a certain temperature. Larger particle domains were of identical phase to the bulk, indicating that small size favours the formation of the beta -form

Further study on double-melting endotherms of isotactic polypropylene

The origins of the single- and double-melting endotherms of isotactic polypropylene crystallized at different temperatures were studied carefully by differential scanning calorimetry, wide-angle X-ray diffraction, and small-angle X-ray scattering. The experimental data show that spontaneous crystallization occurs when the crystallization temperature is lower than 117 degrees C; thus the lamellae formed are imperfect. At a lower heating rate, the recrystallization or reorganization of these imperfect lamellae leads to double endotherms. On the other hand, when the crystallization temperature is higher than 136 degrees C, two major kinds of lamellae with different thickness are developed during the isothermal process, which also results in the double-melting endotherms. In the intermediate temperature range the lamellae formed are perfect, and there is only a single peak in the distribution of lamellar thickness. This explains the origin of the single-melting endotherm

The crystallization behavior of the metastable melts of poly(ethylene terephthalate) from the multiple melting process

During heating of semicrystalline PET, a metastable melt forms far below the equilibrium melting temperature. Crystallization kinetics of this metastable melt is discussed on the basis of DSC results. From the metastable melt almost one-dimensional growth of the crystal occurs through heterogeneous nucleation.

Isothermal crystallization kinetics of PEO in poly(ethylene terephthalate)–poly(ethylene oxide) segmented copolymers. I. Effect of the soft‐block length

The isothermal crystallization kinetics of poly(ethylene oxide) (PEO) block in two poly(ethylene terephthalate) (PET)-PEO segmented copolymers was studied with differential scanning calorimetry. The Avrami equation failed to describe the overall crystallization process, but a modified Avrami equation, the Q equation, did. The crystallizability of the PET block and the different lengths of the PEO block exerted strong influences on the crystallization process, the crystallinity, and time final morphology of the PEO block. The mechanism of nucleation and the growth dimension of the PEG block were different because of the crystallizability of time PET block and the compositional heterogeneity. The crystallization of the PEO block was physically constrained by the microstructure of time PET crystalline phase, which resulted in a lower crystallization rate. However, this influence became weak with the increase in the soft-block length

Lamellar single crystals of nylon-10,10 grown from a dimethylformamide solution

A new solvent, dimethylformamide (DMF), and the traditional solvent, 1,4-butanediol, were used to prepare single crystals of nylon-10,10 from a dilute solution. The lamellae grown from DMF inhabited a more perfect structure and regular shape than those crystals crystallized from traditional solvents such as 1,4-butanediol and glycerin. These thin and perfect lamellar crystals demonstrated patterns of variation in spacing different from those of melt-crystallized spherulites on heating. Specifically, the two main spacings slightly separated rather than continuously approaching each other when the temperature was greater than 180 degreesC. This is a novel phenomenon observed in nylons. Nevertheless, the usual pattern of change in spacing was observed during the cooling process. These lamellar crystals showed more compact spacing of the (002) and (010/100) planes than spherulites at room temperature

Crystallization and melting behavior of amorphous poly(iminosebacoyl iminodecamethylene)

Multiple melting behavior was observed in the differential scanning calorimetry (DSC) scans for the isothermally crystallized poly(iminosebacoyl iminodecamethylene) (PA1010) samples. Coexistence of crystal populations with different lamellar thickness in PA1010 was discussed by means of DSC, wide-angle X-ray diffraction (WAXD), and small-angle X-ray scattering techniques. During crystallization of the polymer, a major lamellar crystal population developed first, which possessed a higher melting temperature. However, a small fraction of the polymer formed minor crystal population with thinner lamellae, which was metastable and, upon post-annealing, could grow into more stable and thicker lamellae through melting and recrystallization process. Lamellae insertion or stacks would develop during the post-annealing at a lower temperature for the isothermally crystallized samples; thus, multiple crystal populations with different thickness could be produced. It is the multiple distribution of lamella thickness that gives rise to multiple melting behavior of crystalline polymers

Physical aging and crystallization of amorphous poly(aryl ether ether ketone ketone)

Physical aging of poly(aryl ether ether ketone ketone) (PEEKK) was investigated. Heat flow responses were measured after annealing the amorphous samples that were obtained by quenching the melt into an ice-water bath at just below the glass transition temperature. Isothermal cold crystallization of the aged samples was carried out. The Avrami equation was used to determine the kinetic parameters, and the Avrami constant it is about 2. An Arrhenius form was used to evaluate the relaxation activation energy of physical aging and the transport activation energy of isothermal crystallization. The activation energy of physical aging was similar in magnitude to that observed for the temperature dependence of crystallization under conditions of transportation control. Results obtained were interpreted as purely kinetic effects associated with the glass formation process

Morphology and structure of poly(aryl ether ketone ketone) containing isophthaloyl moieties crystallized from dilute solution

Spherulites and lamellar single crystals of poly(aryl ether ketone ketone) containing isophthaloyl moieties (PEKK(I)) were obtained from dilute α-chloronaphthalene solution. The morphology and structure of the spherulites and single crystals were studied by electron microscopy and electron diffraction. The spherulites were found to consist of elongated lamellar branches that grow with the b crystallographic axis in the radial direction. Single crystals possess a similar habit, with b parallel to the long axis, a transverse, and c perpendicular to the lamellae plane. High-resolution images of the PEKK(I) crystals which show the perfection of and defects in the crystals, were obtained, and many defects or dislocations were observed.