Efficiency enhancement in dye sensitized solar cells using gel polymer electrolytes based on a tetrahexylammonium iodide and MgI2 binary iodide system

Quasi-solid-state dye-sensitized solar cells have drawn the attention of scientists and technologists as a potential candidate to supplement future energy needs. The conduction of iodide ions in quasi-solid-state polymer electrolytes and the performance of dye sensitized solar cells containing such electrolytes can be enhanced by incorporating iodides having appropriate cations. Gel-type electrolytes, based on PAN host polymers and mixture of salts tetrahexylammonium iodide (Hex4N(+)I(-)) and MgI2, were prepared by incorporating ethylene carbonate and propylene carbonate as plasticizers. The salt composition in the binary mixture was varied in order to optimize the performance of solar cells. The electrolyte containing 120% Hex4N(+)I(-) with respect to weight of PAN and without MgI2 showed the highest conductivity out of the compositions studied, 2.5 × 10(-3) S cm(-1) at 25 °C, and a glass transition at -102.4 °C. However, the electrolyte containing 100% Hex4N(+)I(-) and 20% MgI2 showed the best solar cell performance highlighting the influence of the cation on the performance of the cell. The predominantly ionic behaviour of the electrolytes was established from the dc polarization data and all the electrolytes exhibit iodide ion transport. Seven different solar cells were fabricated employing different electrolyte compositions. The best cell using the electrolyte with 100% Hex4N(+)I(-) and 20% MgI2 with respect to PAN weight showed 3.5% energy conversion efficiency and 8.6 mA cm(-2) short circuit current density.

Phthaloylchitosan-Based Gel Polymer Electrolytes for Efficient Dye-Sensitized Solar Cells

Phthaloylchitosan-based gel polymer electrolytes were prepared with tetrapropylammonium iodide, Pr 4 NI, as the salt and optimized for conductivity. The electrolyte with the composition of 15.7 wt.% phthaloylchitosan, 31.7 wt.% ethylene carbonate (EC), 3.17wt.% propylene carbonate (PC), 19.0 wt.% of Pr 4 NI, and 1.9wt.% iodine exhibits the highest room temperature ionic conductivity of 5.27 x 10 -3 S cm -1. The dye-sensitized solar cell (DSSC) fabricated with this electrolyte exhibits an efficiency of 3.5% with.. SC of 7.38mAcm -2,.. OC of 0.72V, and fill factor of 0.66. When various amounts of lithium iodide (LiI) were added to the optimized gel electrolyte, the overall conductivity is observed to decrease. However, the efficiency of the DSSC increases to a maximum value of 3.71% when salt ratio of Pr 4 NI : LiI is 2 : 1. This cell has.. SC,.. OC and fill factor of 7.25mAcm -2, 0.77V and 0.67, respectively.

Effect of the alkaline cation size on the conductivity in gel polymer electrolytes and their influence on photo electrochemical solar cells

The nature and concentration of cationic species in the electrolyte exert a profound influence on the efficiency of nanocrystalline dye-sensitized solar cells (DSSCs). A series of DSSCs based on gel electrolytes containing five alkali iodide salts (LiI, NaI, KI, RbI and CsI) and polyacrylonitrile with plasticizers were fabricated and studied, in order to investigate the dependence of solar cell performance on the cation size. The ionic conductivity of electrolytes with relatively large cations, K(+), Rb(+) and Cs(+), was higher and essentially constant, while for the electrolytes containing the two smaller cations, Na(+) and Li(+), the conductivity values were lower. The temperature dependence of conductivity in this series appears to follow the Vogel-Tamman-Fulcher equation. The sample containing the smallest cation shows the lowest conductivity and the highest activation energy of ∼36.5 meV, while K(+), Rb(+) and Cs(+) containing samples show an activation energy of ∼30.5 meV. DSSCs based on the gel electrolyte and a TiO2 double layer with the N719 dye exhibited an enhancement in the open circuit voltage with increasing cation size. This can be attributed to the decrease in the recombination rate of electrons and to the conduction band shift resulting from cation adsorption by TiO2. The maximum efficiency value, 3.48%, was obtained for the CsI containing cell. The efficiencies shown in this study are lower compared to values reported in the literature, and this can be attributed to the use of a single salt and the absence of other additives, since the focus of the present study was to analyze the cation effect. The highest short circuit current density of 9.43 mA cm(-2) was shown by the RbI containing cell. The enhancement of the solar cell performance with increasing size of the cation is discussed in terms of the effect of the cations on the TiO2 anode and ion transport in the electrolyte. In liquid electrolyte based DSSCs, the short circuit current density has been reported to decrease with the increasing size of the cation. However, in this work, it follows an opposite trend highlighting a major difference between liquid and quasi-solid electrolytes on the solar cell performance.

Performance enhancers for gel polymer electrolytes based on LiI and RbI for quasi-solid-state dye sensitized solar cells

In this study, the effect of additives (enhancers) on efficiency enhancement in dye sensitized solar cells (DSSCs) containing two series of gel polymer electrolytes, one based on LiI and the other based on RbI have been systematically studied. Polyacrylonitrile (PAN) was used as the host polymer while the performance enhancers used in each case were tetrapropylammoniumiodide (Pr4NI), the ionic liquid 1-methyl-3-propyl imidazolium iodide (MPII) and 4-tert-butylpyridine (4TBP) respectively. Appropriate amounts of the selected enhancers were incorporated one by one, in LiI based and RbI based gel electrolytes. The incorporation of Pr4NI and MPII led to an increase in conductivity of the electrolyte, while 4TBP showed a decrease in conductivity. The maximum conductivity of 3.85 mS cm−1 at room temperature was shown by the RbI based-series while for the LiI based series the maximum conductivity was 2.95 mS cm−1. Each of these electrolytes with respective additives was used to fabricate quasi-solid state DSSCs. For the DSSCs based on the LiI containing series, a significant short circuit current density (Jsc) enhancement (161%) from 3.65 to 9.54 mA cm−2 was observed due to the addition of Pr4NI. This Jsc value further increased to 9.7 mA cm−2 due to the addition of MPII and 4TBP. For the DSSCs with corresponding Rb based electrolytes with all three additives, the highest Jsc value obtained was 11.5 mA cm−2. The incorporation of the three additives Pr4NI, MPII and 4TBP collectively enhanced the open circuit voltages and the efficiencies of both LiI and RbI containing quasi-solid state DSSCs. Another important finding from this work is that rarely used RbI containing electrolytes exhibit superior DSSC performance compared to more frequently used LiI based electrolytes. Hence, RbI appears to be a better candidate compared to LiI to fabricate gel polymer electrolytes for DSSCs in general. The three additives have contributed to a remarkable efficiency enchantment in DSSCs by 449.3% for the LiI based electrolyte and by 35.7% for the RbI based electrolyte.

Rheological behavior of PAN-based electrolytic gel containing tetrahexylammonium and magnesium iodide for photoelectrochemical applications

Polymeric gel electrolyte systems have gained great interest in the last few years due to their suitability for the manufacturing of ionic devices, for example, for dye-sensitized solar cells (DSSCs). In this work, the rheological behavior at fixed temperatures and at fixed frequency of complex systems based on polyacrylonitrile (PAN) and plasticizers such as ethylene carbonate (EC) and propylene carbonate (PC) containing tetrahexylammonium (Hex4NI) and magnesium iodide (MgI2) was studied. These results for these PAN-EC-PC gels suggest a structural change of the “strong-to-weak” type at about 60 °C and the beginning of the gel–sol transition at about 75 °C. These transitions occur at higher temperatures for polymer electrolyte gels containing Hex4NI and even higher with MgI2, suggesting the possibility of post-factum treatments of the gels and of the DSSCs to improve their performance. The rheological results suggest that the progressive substitution of Hex4NI with MgI2leads to a significant improvement in the rheological behavior of the PAN-based electrolytic gel due to the decrease of the mobility of the macromolecules and probably to an increase of the interaction between the inorganic ions and the macromolecules. Moreover, when these gels were used in DSSCs, the sample containing 80(Hex4NI)/40(MgI2) showed the best performance considering its rheological and calorimetric behavior as well as energy conversation efficiency and short-circuit current density.

Dependence of solar cell performance on the nature of alkaline counterion in gel polymer electrolytes containing binary iodides

Performance of dye-sensitized nano-crystalline TiO2 thin film-based photo-electrochemical solar cells (PECSCs) containing gel polymer electrolytes is largely governed by the nature of the cation in the electrolyte. Dependence of the photovoltaic performance in these quasi-solid state PECSCs on the alkaline cation size has already been investigated for single cation iodide salt-based electrolytes. The present study reports the ionic conductivity dependence on the nature of alkaline cations (counterion) in a gel polymer electrolyte based on binary iodides. Polyacrylonitrile-based gel polymer electrolyte series containing binary iodide salts is prepared using one of the alkaline iodides (LiI, NaI, KI, RbI, and CsI) and tetrapropylammonium iodide (Pr4NI). All the electrolytes based on binary salts have shown conductivity enhancement compared to their single cation counterparts. When combined with Pr4NI, each of the Li+, Na+, K+, Rb+, and Cs+ cation containing iodide salts incorporated in the gel electrolytes has shown a room temperature conductivity enhancement of 85.59, 12.03, 12.71, 20.77, and 15.36%, respectively. The conductivities of gel electrolytes containing binary iodide systems with Pr4NI and KI/RbI/CsI are higher and have shown values of 3.28, 3.43, and 3.23 mS cm−1, respectively at room temperature. The influence of the nature of counterions on the performance of quasi-solid state dye-sensitized solar cells is investigated by assembling two series of cells. All the binary cationic solar cells have shown more or less enhancements of open circuit voltage, short circuit current density, fill factor, and efficiency compared to their single cation counterparts. This work highlights the importance of employing binary cations (a large and a small) in electrolytes intended for quasi-solid state solar cells. The percentage of energy conversion efficiency enhancement shown for the PECSCs made with electrolytes containing Pr4NI along with Li+, Na+, K+, Rb+, and Cs+ iodides is 260.27, 133.65, 65.27, 25.32, and 8.36%, respectively. The highest efficiency of 4.93% is shown by the solar cell containing KI and Pr4NI. However, the highest enhancements of ionic conductivity as well as the energy conversion efficiency were exhibited by the PECSC made with Li+-containing binary cationic electrolyte.