Synthesis of Nanosheet Crystallites of Ruthenate with an α-NaFeO2-Related Structure and Its Electrochemical Supercapacitor Property

Unilamellar crystallites of conductive ruthenium oxide having a thickness of about 1 nm were obtained via elemental exfoliation of a protonic layered ruthenate, H(0.2)RuO(2).0.5H(2)O, with an alpha-NaFeO(2)-related crystal structure. The obtained RuO(2) nanosheets possessed a well-defined crystalline structure with a hexagonal symmetry, reflecting the crystal structure of the parent material. The restacked RuO(2) nanosheets exhibited a high pseudocapacitance of approximately 700 F g(-1) in an acidic electrolyte, which is almost double the value of the nonexfoliated layered protonated ruthenate.

Fabrication of ruthenium metal nanosheets via topotactic metallization of exfoliated ruthenate nanosheets

The metallization behavior of molecularly thin RuO2 nanosheets obtained from complete delamination of layered ruthenates was studied. Interestingly, the RuO2 nanosheets in a monolayer state topotactically transformed into a single layer of Ru atoms, i.e., ruthenium metal nanosheets, which can be regarded as a new family of nanosized metals.