Telma Nunes do Nascimento

Shear bond strength of enamel surface treated with air-abrasive system

The aim of this study was to evaluate the shear bond strength of a composite resin to dental enamel, using three different surface treatments. Fifteen sound third molars were randomly assigned to three groups. The mesial and distal surfaces were flattened and covered using adhesive tape with a central orifice delimiting the adhesion area (7.07 mm2). Group I, the enamel surface was conditioned with 37% phosphoric acid for 15 s; group II, the surface was treated using air abrasion with aluminum oxide; group III, the enamel surface was treated using an association of air abrasion with aluminum oxide and 37% phosphoric acid. The Single Bond (3M) adhesive system was applied and a Teflon matrix was placed and filled with composite resin Z-100 (3M) and light-cured. The shear bond strength test was performed with a universal testing machine. The acid etching technique and air abrasion with aluminum oxide associated with acid etching had the highest shear bond strength values. Data were subjected to statistical analysis using ANOVA and the Turkey test, and no statistically significant difference in shear bond strength was observed between group I (12.49 +/- 2.85 MPa) and group III (12.59 +/- 2.68 MPa). In contrast, both groups had statistically better shear bond strengths compared to group II (0.29 +/- 0.56 MPa; p < 0.05). Air abrasion with aluminum oxide does not substitute acid etching. The association of these methods to obtain adequate adhesion to the substrate is necessary.

Effect of air abrasion on tensile bond strength of a single-bottle adhesive/indirect composite system to enamel

This study evaluated the efficiency of air abrasion alone and associated with phosphoric acid etching on tensile bond strength of a single-bottle adhesive/indirect composite restorative system (Bond 1/Alert) to human enamel. Forty enamel surfaces from extracted human third molars were assigned to 4 groups (n= 10). Mach 4.1 (Kreativ Inc.) air abrasion equipment was used for 20 s. A special system of rod pairs aligned in a specific apparatus was used for tensile strength tests, according to ISO/TR 11405 standard (1994) with some modifications. Bond strength means were: G1 (air abrasion + rinsing + condensable composite resin Alert) = 3.46 +/- 0.83 MPa; G2 (air abrasion + rinsing + Bond 1 adhesive system + Alert) = 4.00 +/- 1.60 MPa; G3 (air abrasion + rinsing + 37% phosphoric acid + rinsing + Bond 1 + Alert) = 20.80 +/- 3.95 MPa; and G4 (37% phosphoric acid + rinsing + Bond 1 + Alert) = 17.00 +/- 2.74 MPa. The statistical analysis by Kruskal-Wallis test revealed that G1 and G2 presented statistically significant difference (p< 0.05) from G3 and G4 (p<0.01) and G1 and G3 did not differ significantly (p> 0.05) from G2 and G4, respectively.