Microstructural Characteristics of Accumulative Roll-Bonded Ni-Al-Based Metal-Intermetallic Laminate Composite

The present investigation is an attempt to develop metal-intermetallic laminate composites based on Ni-Al system. In this study, Ni sheets and Al foils have been used for the development of Ni-Al laminate using accumulative roll-bonding technique at 773xa0K. The laminate composites were then subjected to the controlled annealing to affect reactive diffusion at the Ni/Al interface leading to intermetallic compound formation. The accumulative roll-bonded laminates showed good bonding of layers. Annealing treatment at 773xa0K led to formation of reaction product and maintained the interface integrity. A qualitative compositional analysis at the interfaces reflected the formation of Al-Ni compounds, and a gradual compositional gradient also across the interface. This process seems to be of promise so far as the continuous production of large scale metal-intermetallic laminate composites is concerned.

Effect of High-Temperature Severe Plastic Deformation on Microstructure and Mechanical Properties of IF Steel

Extensive research work has been carried out on interstitial-free steel to understand its response to deformation; particularly, the behavior during severe plastic deformation (SPD). However, most of these studies were mainly undertaken in the ferritic regime. The present investigation reports the initial results of our attempt to employ accumulative roll bonding (ARB), one of the variants of SPD, at a high temperature (950xa0°C). A considerable grain refinement has been observed, which may be attributed to the severity of deformation and recrystallisation at high temperatures. Nanoindentation tests have been performed at various stages of ARB process to understand the evolution of mechanical properties.