W. H. Lim

Graphene oxide-based waveguide polariser: from thin film to quasi-bulk

We have demonstrated a broadband waveguide polariser with high extinction ratio on a polymer optical waveguide coated with graphene oxide via the drop-casting method. The highest extinction ratio of nearly 40 dB is measured at 1590 nm, with a variation of 4.5 dB across a wavelength range from 1530 nm to 1630 nm, a ratio that is (to our knowledge) the highest reported for graphene-based waveguide polarisers to date. This result is achieved with a graphene oxide coating length along the propagation direction of only 1.3 mm and a bulk film thickness of 2.0 µm. The underlying principles of the strongly polarisation dependent propagation loss demonstrated have been studied and are attributed to the anisotropic complex dielectric function of graphene oxide bulk film.

Reflection spectra of etched FBGs under the influence of axial contraction and stress-induced index change

We present a new theoretical model for the broadband reflection spectra of etched FBGs which includes the effects of axial contraction and stress-induced index change. The reflection spectra of the etched FBGs with several different taper profiles are simulated based on the proposed model. In our observation, decaying exponential profile produces a broadband reflection spectrum with good uniformity over the range of 1540-1560 nm. An etched FBG with similar taper profile is fabricated and the experimental result shows good agreement with the theoretical model.

Note: Fabrication of tapered fibre tip using mechanical polishing method

Tapered fibre tips fabricated using mechanical polishing method is studied. The fibre tips are formed by sequential polishing flat-ended single mode fibres with decreasing aluminium oxide polishing film grit size. Based on the proposed technique, tapered fibre tips with cone angle ranging from 30° to 130° are fabricated by controlling the polishing angle. Besides the variety of cone angle, considerable smoothness of the fibre tip surface may assist in good metal coating and hence a well-defined aperture can be obtained. In addition, this paper presents a two-step hybrid fabrication method combining the proposed polishing method with chemical etching method to increase the possible fibre tip cone angles achievable by chemical etching method.

Photo-induced reduction of graphene oxide coating on optical waveguide and consequent optical intermodulation

Increased absorption of transverse-magnetic (TM) - polarised light by a graphene-oxide (GO) coated polymer waveguide has been observed in the presence of transverse-electric (TE) - polarised light. The GO-coated waveguide exhibits very strong photo-absorption of TE-polarised light - and acts as a TM-pass waveguide polariser. The absorbed TE-polarised light causes a significant temperature increase in the GO film and induces thermal reduction of the GO, resulting in an increase in optical-frequency conductivity and consequently increased optical propagation loss. This behaviour in a GO-coated waveguide gives the action of an inverted optical switch/modulator. By varying the incident TE-polarised light power, a maximum modulation efficiency of 72% was measured, with application of an incident optical power level of 57 mW. The GO-coated waveguide was able to respond clearly to modulated TE-polarised light with a pulse duration of as little as 100 μs. In addition, no wavelength dependence was observed in the response of either the modulation (TE-polarised light) or the signal (TM-polarised light).