Xingfeng Lei

Hyperbranched polysiloxane (HBPSi)-based polyimide films with ultralow dielectric permittivity, desirable mechanical and thermal properties

Low-dielectric polyimide (PI) is on high demand in the next generation of high-density and high-speed integrated circuits. The introduction of fluorine or pores into PIs has been reported to efficiently obtain low-dielectric properties, but unavoidably deteriorate the mechanical and/or thermal properties. Therefore, it is a great challenge for PI to decrease its Dk and simultaneously maintain its mechanical and thermal properties. Herein, a series of robust PI films were fabricated by copolymerizing amine-functionalized hyperbranched polysiloxane (HBPSi) with pyromellitic dianhydride (PMDA) and 4,4′-oxydianiline (ODA). The outstanding dielectric properties were achieved in a 35 wt% HBPSi PI film, which exhibits a Dk as low as 2.24 (1 MHz), mainly owing to the enhanced free volume and dielectric confinement effect afforded by the bulky HBPSi. Meanwhile, 35 wt% HBPSi PI demonstrates remarkable thermal stability and admirable mechanical properties, with the glass transition temperature of 388 °C, 5% weight loss temperature in argon flow up to 554 °C, a tensile strength of 80.6 MPa, elongation at break of 13.7% and a tensile modulus of 1.36 GPa. It also demonstrates conspicuous film homogeneity and planarity with the surface roughness as low as 0.42 nm and good moisture resistance with water uptake less than 1.5%. The prominent comprehensive properties make HBPSi PI a strong candidate for the future interlayer dielectrics.

Synthesis of BSA/Fe3O4 magnetic composite microspheres for adsorption of antibiotics

BSA/Fe3O4 magnetic composite microspheres with high saturation magnetization and paramagnetic property were prepared via inverse emulsion technology at room temperature, bovine serum albumin (BSA, 60 KD), magnetic nanoparticles (Fe3O4) and glutaraldehyde as macromonomer, inorganic particles and cross-linking agent, respectively. Fourier transform infrared (FTIR), scanning electron microscope (SEM), metalloscope, and particle size analyzer were used to characterize morphology and structure of composite microspheres. Vibrating sample magnetometer (VSM) and thermogravimetric analysis (TGA) were used to test magnetic properties of the synthesized samples, adsorption capacity of microspheres was determined by ultraviolet spectrophotometer (UV). The results showed that BSA/Fe3O4 microspheres were 43 μm with relatively narrow particle size distribution, perfect sphere-shaped morphologies, superparamagnetism with a saturation magnetization of 11 emu/g, and high magnetic content with a value of 57.29%. The main factors influencing properties of microspheres including raw material ratio, the amount of emulsifier and cross-linking agent, agitation speed were investigated and optimized. Furthermore, these microspheres accompanying with high separable and reusable efficient may have great potential application in the field of separation, in particular, removal of antibiotics. Adsorption capacities of the microspheres of four different kinds of antibiotics (erythromycin, streptomycin, tetracycline and chloramphenicol) ranging from 69.35 mg/g to 147.83 mg/g were obtained, and Langmuir isotherm model coincided with equilibrium data than that of the Freundlich model.

Atomic oxygen resistance of polyimide/silicon hybrid thin films with different compositions and architectures

Silicon (Si)-containing polyimides (PIs) with superior atomic oxygen (AO) resistance are promising materials for space applications. Here, in this study, we present the synthesis and characterization of eight Si-containing PI thin films and evaluate their AO durability. The resulting PI films exhibited high thermal stability and preferable AO resistance but showed slightly reduced mechanical performance relative to pristine PI. The highest optical transparency at 550 nm was observed for PI/octaaminopropylsilsesquioxane, while the lowest value was observed for PI/silica (SiO2) hybrids. X-Ray photoelectron spectroscopic study suggested that the topmost surface of PI was degraded at the early stage and an SiO2 inert protective layer was finally formed on the surface of hybrid films after AO exposure. It is found that Si-containing units of higher oxidation states and with higher Si/O molar ratio are favorable to improve the AO resistance. Dispersion of Si at molecular level contributes to improving anti-AO property as well as optical transparency of the prepared films. The characterization of scanning electron microscopy indicated a continuous SiO2 protective layer was crucial to prevent AO from eroding the bulk matrix.

Application of yolk–shell Fe3O4@N-doped carbon nanochains as highly effective microwave-absorption material

Yolk–shell Fe3O4@N-doped carbon nanochains, intended for application as a novel microwave-absorption material, have been constructed by a three-step method. Magnetic-field-induced distillation-precipitation polymerization was used to synthesize nanochains with a one-dimensional (1D) structure. Then, a polypyrrole shell was uniformly applied to the surface of the nanochains through oxidant-directed vapor-phase polymerization, and finally the pyrolysis process was completed. The obtained products were characterized by X-ray diffraction (XRD), X-ray photoelectron spectra (XPS), and thermogravimetric analyses (TGA) to confirm the compositions. The morphology and microstructure were observed using an optical microscope, scanning electron microscope (SEM), and transmission electron microscope (TEM). The N2 absorption–desorption isotherms indicate a Brunauer–Emmett–Teller (BET) specific surface area of 74 m2/g and a pore width of 5–30 nm. Investigations of the microwave absorption performance indicate that paraffin-based composites loaded with 20 wt.% yolk–shell Fe3O4@N-doped carbon nanochains possess a minimum reflection loss of −63.09 dB (11.91 GHz) and an effective absorption bandwidth of 5.34 GHz at a matching layer thickness of 3.1 mm. In addition, by tailoring the layer thicknesses, the effective absorption frequency bands can be made to cover most of the C, X, and Ku bands. By offering the advantages of stronger absorption, broad absorption bandwidth, low loading, thin layers, and intrinsic light weight, yolk–shell Fe3O4@N-doped carbon nanochains will be excellent candidates for practical application to microwave absorption. An analysis of the microwave absorption mechanism reveals that the excellent microwave absorption performance can be explained by the quarter-wavelength cancellation theory, good impedance matching, intense conductive loss, multiple reflections and scatterings, dielectric loss, magnetic loss, and microwave plasma loss.