Y.L. Huang

Effects of intergranular phase on the coercivity for MnBi magnets prepared by spark plasma sintering

MnBi magnets with a high content of low temperature phase (LTP) and excellent magnetic properties were prepared by spark plasma sintering (SPS) using ball milling powders as precursors without magnetic purification. A complicated intergranular phase, which contains Mn phase, Bi phase, MnO phase, and even amorphous phase in MnBi magnets, was characterized and reported systematically. It was found that the formation of intergranular phase which was contributed by ball milling precursors and sintering mechanism, jointly, had important influence on the magnetic properties. The appropriate content of intergranular phase was beneficial in improving the coercivity due to the strong magnetic isolation effects. The optimum magnetic properties with Mr=26.0 emu/g, Hci= 7.11 kOe and (BH)max=1.53 MGOe at room temperature, and a maximum value Hci= 25.37 kOe at 550 K can be obtained. Strongly favorable magnetic properties make SPSed MnBi magnets an attractive candidate material for small permanent magnets used in high-temperature applications.MnBi magnets with a high content of low temperature phase (LTP) and excellent magnetic properties were prepared by spark plasma sintering (SPS) using ball milling powders as precursors without magnetic purification. A complicated intergranular phase, which contains Mn phase, Bi phase, MnO phase, and even amorphous phase in MnBi magnets, was characterized and reported systematically. It was found that the formation of intergranular phase which was contributed by ball milling precursors and sintering mechanism, jointly, had important influence on the magnetic properties. The appropriate content of intergranular phase was beneficial in improving the coercivity due to the strong magnetic isolation effects. The optimum magnetic properties with Mr=26.0 emu/g, Hci= 7.11 kOe and (BH)max=1.53 MGOe at room temperature, and a maximum value Hci= 25.37 kOe at 550 K can be obtained. Strongly favorable magnetic properties make SPSed MnBi magnets an attractive candidate material for small permanent magnets used in high-t...

Magnetic and Magnetocaloric Properties in Ferrimagnetic Mn 2− x Co x Sb (

The ferrimagnetic Mn2-xCoxSb (x = 0.15 and 0.20) alloys were prepared by arc-melting technique. The structure, magnetic, and magnetocaloric properties on these compounds were investigated. The tetragonal Cu2Sb-type structure (P4/nmm space group) was confirmed by X-ray powder diffraction measurements at room temperature for these two alloys. The Co-introduction results in a first-order magnetic transition between the antiferromagnetic and the ferrimagnetic state. Adopting the standard and loop process method, respectively, the measurements of isothermal magnetization were performed and the magnetic entropy changes were evaluated for these alloys.