A porous sintered material consisting of Presep PolyChelate as a chelating resin and particulate polyethylene as a thermoplastic binder for solid-phase extraction of trace elements

Cylinder-type and disk-type sintered materials consisting of Presep PolyChelate, which is a commercially available chelating resin immobilizing carboxymethylated polyethyleneimine as a functional group, and particulate polyethylene as a thermoplastic binder were prepared using a polymer sintering technique. The sintered materials had a continuously porous structure. The sintering process at 130u202f°C for 20u202fmin did not affect the ability of the chelating resin in the sintered materials; the selectivity of the sintered material was almost the same as that of the particulate chelating resin which was not sintered. The sintering materials could quantitatively extract 11 kinds of trace elements, namely Cd, Co, Cu, Fe, Mn, Mo, Ni, Pb, Ti, V, and Zn, at pH 5.5. When the disk-type sintered material was used, the recoveries of these elements remained almost constant at a flow rate of at least 50u202fmLu202fmin-1; the extracted elements could be eluted using 10u202fmL of 3u202fmolu202fL-1 nitric acid at a flow rate of 5u202fmLu202fmin-1. Solid-phase extraction using the disk-type sintered material was applied to the separation and preconcentration of trace elements prior to their inductively coupled plasma atomic emission spectrometric determination. The method was applicable to analyses of certified reference materials (EnviroMAT ES-L-1 ground water and EU-L-3 waste water) and a commercially available table salt.