Chencheng Xu

Disentanglement of growth dynamic and thermodynamic effects in LaAlO3/SrTiO3 heterostructures.

The influence of non-equilibrium and equilibrium processes during growth of LaAlO3/SrTiO3 (LAO/STO) heterostructures is analyzed. We investigate the electronic properties of LAO/STO heterostructures obtained at constant growth conditions after annealing in different oxygen atmospheres within the typical growth window (1 × 10−4 mbar –1 × 10−2 mbar). The variation of annealing conditions is found to cause a similar change of electronic properties as observed for samples grown in different oxygen pressure. The results indicate that equilibrium defect formation is the dominant process for establishing the properties of the two-dimensional electron gas (2DEG), while growth dynamics play a minor role in the typical LAO/STO growth regime. Furthermore, the effects of non-equilibrium processes occurring during growth are investigated in detail by quenching just-grown LAO/STO heterostructures directly after growth. We show that during growth the sample is pushed into a non-equilibrium state. After growth, the sample then relaxes towards equilibrium, while the relaxation rate strongly depends on the ambient pressure. The observed relaxation behavior is mainly associated with a reoxidation of the STO bulk, while the 2DEG is formed immediately after the growth.

Surface Termination Conversion during SrTiO3 Thin Film Growth Revealed by X-ray Photoelectron Spectroscopy.

Emerging electrical and magnetic properties of oxide interfaces are often dominated by the termination and stoichiometry of substrates and thin films, which depend critically on the growth conditions. Currently, these quantities have to be measured separately with different sophisticated techniques. This report will demonstrate that the analysis of angle dependent X-ray photoelectron intensity ratios provides a unique tool to determine both termination and stoichiometry simultaneously in a straightforward experiment. Fitting the experimental angle dependence with a simple analytical model directly yields both values. The model is calibrated through the determination of the termination of SrTiO3 single crystals after systematic pulsed laser deposition of sub-monolayer thin films of SrO. We then use the model to demonstrate that during homoepitaxial SrTiO3 growth, excess Sr cations are consumed in a self-organized surface termination conversion before cation defects are incorporated into the film. We show that this termination conversion results in insulating properties of interfaces between polar perovskites and SrTiO3 thin films. These insights about oxide thin film growth can be utilized for interface engineering of oxide heterostructures. In particular, they suggest a recipe for obtaining two-dimensional electron gases at thin film interfaces: SrTiO3 should be deposited slightly Ti-rich to conserve the TiO2-termination.

Unraveling the enhanced Oxygen Vacancy Formation in Complex Oxides during Annealing and Growth

The reduction of oxides during annealing and growth in low pressure processes is a widely known problem. We hence investigate the influence of mere annealing and of growth in vacuum systems to shed light on the reasons behind the reduction of perovskites. When comparing the existing literature regarding the reduction of the perovskite model material SrTiO3 it is conspicuous that one finds different oxygen pressures required to achieve reduction for vacuum annealing and for chemically controlled reducing atmospheres. The unraveling of this discrepancy is of high interest for low pressure physical vapor depositions of thin films heterostructures to gain further understanding of the reduction of the SrTiO3. For thermal annealing, our results prove the attached measurement devices (mass spectrometer/ cold cathode gauge) to be primarily responsible for the reduction of SrTiO3 in the deposition chamber by shifting the thermodynamic equilibrium to a more reducing atmosphere. We investigated the impact of our findings on the pulsed laser deposition growth at low pressure for LaAlO3/SrTiO3. During deposition the reduction triggered by the presence of the laser plume dominates and the impact of the measurement devices plays a minor role. During post annealing a complete reoxidization of samples is inhibited by an insufficient supply of oxygen.

Tuning cationic composition of La:EuTiO3−δ films

Eu1−xLaxTiO3−δ (x = 0, 0.3, 0.5) films were deposited in a p(Ar(96%)/H2(4%)) = 4 × 10−4 mbar atmosphere on (LaAlO3)0.3-(Sr2AlTaO6)0.7 vicinal substrates (0.1°). Reflection high-energy electron diffraction oscillation characteristics of a layer-by-layer growth mode were observed for stoichiometric and Ti-rich films and the laser fluence suited to deposit stoichiometric films was identified to be 1.25 J/cm2 independent of the La content. The variety of resulting film compositions follows the general trend of Eu-enrichment for low laser and Ti-enrichment for high laser fluence. X-ray diffraction confirms that all the films are compressively strained with a general trend of an increase of c-axis elongation for non-stoichiometric films. The surfaces of non-stoichiometric films have an increased roughness, the highest sheet resistances, exhibit the presence of islands, and are Eu3+ rich for films deposited at low laser fluence.

Formation mechanism of Ruddlesden-Popper-type antiphase boundaries during the kinetically limited growth of Sr rich SrTiO3 thin films

We elucidated the formation process for Ruddlesden-Popper-type defects during pulsed laser deposition of Sr rich SrTiO3 thin films by a combined analysis of in-situ atomic force microscopy, low energy electron diffraction and high resolution scanning transmission electron microscopy. At the early growth stage of 1.5 unit cells, the excess Sr results in the formation of SrO on the surface, resulting in a local termination change from TiO2 to SrO, thereby forming a Sr rich (2 × 2) surface reconstruction. With progressive SrTiO3 growth, islands with thermodynamically stable SrO rock-salt structure are formed, coexisting with TiO2 terminated islands. During the overgrowth of these thermodynamically stable islands, both lateral as well as vertical Ruddlesden-Popper-type anti-phase boundaries are formed, accommodating the Sr excess of the SrTiO3 film. We suggest the formation of thermodynamically stable SrO rock-salt structures as origin for the formation of Ruddlesden-Popper-type antiphase boundaries, which are as a result of kinetic limitations confined to certain regions on the surface.

UV radiation enhanced oxygen vacancy formation caused by the PLD plasma plume

Pulsed Laser Deposition is a commonly used non-equilibrium physical deposition technique for the growth of complex oxide thin films. A wide range of parameters is known to influence the properties of the used samples and thin films, especially the oxygen-vacancy concentration. One parameter has up to this point been neglected due to the challenges of separating its influence from the influence of the impinging species during growth: the UV-radiation of the plasma plume. We here present experiments enabled by a specially designed holder to allow a separation of these two influences. The influence of the UV-irradiation during pulsed laser deposition on the formation of oxygen-vacancies is investigated for the perovskite model material SrTiO3. The carrier concentration of UV-irradiated samples is nearly constant with depth and time. By contrast samples not exposed to the radiation of the plume show a depth dependence and a decrease in concentration over time. We reveal an increase in Ti-vacancy–oxygen-vacancy-complexes for UV irradiated samples, consistent with the different carrier concentrations. We find a UV enhanced oxygen-vacancy incorporation rate as responsible mechanism. We provide a complete picture of another influence parameter to be considered during pulsed laser depositions and unravel the mechanism behind persistent-photo-conductivity in SrTiO3.

Formation of a conducting LaAlO3/SrTiO3 interface studied by low-energy electron reflection during growth

The two-dimensional electron gas occurring between the band insulators SrTiO

The influence of the local oxygen vacancy concentration on the piezoresponse of strontium titanate thin films.

_3

Impact of cation stoichiometry on the early stage of growth of SrTiO3 deposited by pulsed laser deposition

and LaAlO

In situ studies of the growth and oxidation of complex metal oxides by pulsed laser deposition

_3