Dmitriy Berillo

Formation of macroporous self-assembled hydrogels through cryogelation of Fmoc-Phe-Phe.

In this study, it was found that macroporous hydrogels were formed when self-assembly of fluorenyl-9-methoxycarbonyl (Fmoc)-diphenylalanine (Phe-Phe) peptides was induced using glucono-δ-lactone (GdL) in apparently frozen samples. Formed cryogels exhibited a heterogeneous structure with pore walls of densely packed fibres of assembled dipeptides and pores in the range 10-100 μm. Hydrogels formed from the same composition above the freezing point exhibited a homogenous structure without any apparent porosity. The formed gels were characterised using microscopy techniques, CD-spectroscopy and stress sweeps. The cryogels exhibited less mechanical strength than the hydrogels that might be due to the heterogeneous structure of the former. It appeared that the self-assembled peptide both in the cryo- and hydrogel maintained the β-sheet structure commonly attributed to these.

Microcontact-BSA imprinted capacitive biosensor for real-time, sensitive and selective detection of BSA

Highlights • Microcontact imprinting of proteins on a sensor chip was used.• High sensitivity was observed.• Selectivity was equal to or better than that of antibodies.• Stability of the sensor chip was very high.

Oxidized Dextran as Crosslinker for Chitosan Cryogel Scaffolds and Formation of Polyelectrolyte Complexes between Chitosan and Gelatin

Macroporous scaffolds composed of chitosan and using oxidized dextran as a crosslinker are produced through cryogelation. Introducing gelatin as a third component into the structure results in the formation of mesopores in the pore walls, which are not seen if gelatin is excluded. The mesoporous structure is explained by the formation of polyelectrolyte complexes between chitosan and gelatin before crosslinking takes place. The scaffolds exhibit highly elastic properties withstanding compressions up to 60%. The in vitro biocompatibility of the cryogels is evaluated using fibroblasts from a mouse cell line (L929) and it is seen that the cells adhere and proliferate on the scaffolds. The mesoporous structure seems to have a positive effect on proliferation.

Cryogelation of Chitosan Using Noble-Metal Ions: In Situ Formation of Nanoparticles.

One of the purposes of the project was to develop the method of preparation of 3D macroporous hydrogel with a structure of interconnected pores by the use of noncovalent interactions. The combination of chitosan and noble-metal complexes was investigated as cross-linking agents for the preparation of ionic cryogels (ICs). Furthermore, the treatment of the ICs containing gold complex by glutaraldehyde results in spontaneous formation of gold nanoparticles (AuNPs) and chemical cross-linking of the cryogel. The characterization of prepared macroporous materials was carried out by the use of FTIR, SEM, TEM techniques, and texture analyzer. A new strategy for control of size distribution of AuNPs was suggested. The size distribution of obtained AuNPs and their population inside of walls of cryogels was estimated. A method for quantifying unreacted chloroauric acid in the presence of acetic acid was proposed. The possibility of use of prepared cryogels with immobilized AuNPs as a catalytic flow through reactor is shown.

Enzyme-catalyzed crosslinking in a partly frozen state: a new way to produce supermacroporous protein structures.

In this study a new way to produce supermacroporous protein structures was investigated. Enzyme-mediated crosslinking of gelatin or casein was performed in a partly frozen state, which yielded stable, protein-based cryogels. The reaction kinetics for the formation of cryogels were found to be fairly slow, most likely due to the low temperature (-12 °C) used or due to an increased viscosity owing to the cryo-concentration taking place. The produced cryogels were characterized with regards to their physical properties and in vitro degradation. Furthermore, cryogels produced from gelatin and casein were evaluated as potential scaffolds by fibroblast cultivation to confirm their in vitro biocompatibility. Gelatin- and casein-based scaffolds both supported cell proliferation and migration through the scaffold.

3D-macroporous chitosan-based scaffolds with in situ formed Pd and Pt nanoparticles for nitrophenol reduction

3D-macroporous chitosan-based scaffolds (cryogels) were produced via growth of metal-polymer coordinated complexes and electrostatic interactions between oppositely charged groups of chitosan and metal ions under subzero temperatures. A mechanism of reduction of noble metal complexes inside the cryogel walls by glutaraldehyde is proposed, which produces discrete and dispersed noble metal nanoparticles. 3D-macroporous scaffolds prepared under different conditions were characterised using TGA, FTIR, nitrogen adsorption, SEM, EDX and TEM, and the distribution of platinum nanoparticles (PtNPs) and palladium nanoparticles (PdNPs) in the material assessed. The catalytic activity of the in situ synthesised PdNPs, at 2.6, 12.5 and 21.0 μg total mass, respectively, was studied utilising a model system of 4-nitrophenol reduction. The kinetics of the reaction under different conditions (temperature, concentration of catalyst) were examined, and a decrease of catalytic activity was not observed over 17 treatment cycles. Increasing the temperature of the catalytic reaction from 10 to 22 and 35 °C by PdNPs supported within the cryogel increased the kinetic rate by 44 and 126%, respectively. Turnover number and turnover frequency of the PdNPs catalysts at room temperature were in the range 0.20-0.53 h-1. The conversion degree of 4-nitrophenol at room temperature reached 98.9% (21.0 μg PdNPs). Significantly less mass of palladium nanoparticles (by 30-40 times) was needed compared to published data to obtain comparable rates of reduction of 4-nitrophenol.