Eduardo Peón Avés

Hydroxyapatite coating by sol–gel on Ti–6Al–4V alloy as drug carrier

In this study Ti–6Al–4V samples were used as substrates and Ca–P layers were deposited using sol–gel technique and covered by spin-coating. The efficiency of hydroxyapatite (HA) coatings as drug carrier was also evaluated by immersion in gentamicin sulphate solution and the release profiles were obtained by cumulative method of the coating samples. Three non-linear mathematical methods were employed in order to discuss a possible mechanism to lead the drug release. Physical chemical techniques showed the presence of the typical absorption bands of calcium phosphates by infrared spectroscopy while X-ray diffraction peaks matched up with hydroxyapatite patterns. Microstructural techniques (SEM, EDS) help to confirm the hydroxyapatite coating by surface aspect and Ca/P ratio (1.64). The best fitting according statistical results explained each stage of the released profiles and correspond to a mixture of short initial burst effect plus drug dissolution with a specific kinetic and the diffusion of the gentamicin solid particles.

Comparative study of hydroxyapatite coatings obtained by Sol-Gel and electrophoresis on titanium sheets

A comparative study of two coating methods on titanium (Ti) substrates, sol-gel and electrophoresis processes, was performed. Before coating, two different surface treatments were employed. The hydroxyapatite (HA) powder were characterized by infrared spectroscopy (FTIR) and X-ray diffraction (XRD) while coated samples were examined by using scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS). Both techniques seem to be suitable to coat Ti. A previous surface treatment on metallic titanium seems to be fundamental to enhance coat uniformity and adhesion that was estimated by the adhesive tape test. The decrease in calcination temperature did not affect the coating adhesion.

Radiation Sterilization of a Bifunctional Cement Formulation of Hydroxilapatite‐Plaster‐Polymers

ABSTRACT: A sterilization method based on the use of gamma ionizing radiation was applied to a cement formulation of hydroxilapatite, plaster and polymers to be used in bone restorations in dental, aesthetic, and neurological surgery. After the cement was exposed to a dose of 21.5 kGy it reached the sterility assurance level which was necessary for its employment in surgical applications as specified by International Standard ISO ordinate 11137: Radiation Sterilization of Health Care Products. No variation in the initial cement composition or processing parameters, such as working or setting time and molding quality was observed due to sterilization. Its characteristics as a drug delivery system were also not affected. Therefore, radiation sterilization provides a feasible alternative to conventional sterilization methods such as dry/wet heat and ethylene oxide.

Recobrimento da liga Ti-6Al-4V com hidroxiapatita pelo método sol-gel e sua aplicação a hastes femorais não-cimentadas

The coating of metallic alloys with bioactive ceramics aims to accelerate bone formation around the implant, contributing to its fixation. In this paper, the deposition of hydroxyapatite ceramic on Ti-6Al-4V alloy sheets by the sol-gel method was studied. The coating layer was characterized by scanning electron microscopy, X-ray diffraction and its adhesion to substrate was evaluated by shear testing. The citocompatibility test shows that the sol-gel coating did not provoke the cell death significantly higher than the control (p > 0.05). Moreover, femoral stems removed from patient (explants) were adequately coated using the sol-gel process.