Antibacterial activity, surface roughness, flexural strength, and solubility of conventional luting cements containing chlorhexidine diacetate/cetrimide mixtures

STATEMENT OF PROBLEM The failure of fixed dental restorations is commonly associated with caries. The use of conventional luting cements containing antibacterial agents may overcome this problem. PURPOSE The purpose of this study was to evaluate the antibacterial activity (ABA), surface roughness (Ra), flexural strength (FS), and solubility (SL) patterns of the conventional dental luting cements zinc phosphate (ZP), zinc polycarboxylate (PC), and glass ionomer (GIC) after the addition of 5% chlorhexidine diacetate/cetrimide (CHX+CT). MATERIAL AND METHODS Antibacterial agents with a total concentration of 5% (2.5% CHX+2.5% CT) were added to antibacterial agent-free conventional luting cement powders (ZPC, PCC, and GICC) and designated as experimental groups (ZPE, PCE, and GICE). ABA against Streptococcus mutans (SM) and Lactobacillus casei (LB) was examined by using the agar diffusion test method. Ra, FS, and SL values were obtained after storage in distilled water at 37°C for 24 hours. The Kruskal-Wallis and Mann Whitney U with Bonferroni correction tests were used to test for agar diffusion (α=.05) and 2-way ANOVA and Fisher Least Significant Difference (LSD) test were used to measure Ra, FS, and SL (α=.05). RESULTS The control groups exhibited limited ABA. With the exception of PCE>PCC on day 1 for SM, all experimental groups showed significantly greater and longer-lasting protection against SM and LB bacteria for up to 180 days than their controls (P<.05). Ra values decreased (ZPC>ZPE; P>.05, PCC>PCE; P<.05) except that GICE>GICC (P>.05) when compared with their individual controls. Control groups exhibited higher FS values than did the experimental groups (ZPC>ZPE; P<.05, PCC>PCE; P<.05, GICC>GICE; P>.05). The experimental groups exhibited higher solubilities than did their controls in the ZPC (P>.05) and GICC groups (P<.05) but were lower in PCC group (P<.05). CONCLUSIONS Incorporating a 5% CHX+CT mixture into conventional dental luting cements and altering their Ra, FS, and SL values may provide greater antibacterial protection against SM and LB.

Discoloration of provisional restorations after oral rinses.

Purpose: Oral rinses are widely used to promote periodontal health with provisional restorations during the interim period. The aim of this study was to compare the discoloration of provisional restoration materials with different oral rinses. Material and Methods: A total of 140 disc-shaped specimens (shade A2) (10 mm x 2 mm) were prepared from one PMMA-based (TemDent Classic®) and three different bis-acrylic-based (Protemp II®, Luxatemp® and Fill-In®) provisional restoration materials (n=7). The color values (L*, a*, and b*) of each specimen were measured before and after exposure with a colorimeter, and the color changes (∆E) were calculated according to the CIE L*a*b* system. The specimens were immersed in each of the 4 oral rinses (alcohol-containing mouthwash, chlorhexidine, benzydamine HCl, benzydamine HCl and chlorhexidine) twice a day for 2 minutes. After 2 minutes of immersion in the oral rinses, the specimens were immersed in artificial saliva. The specimens were exposed to the oral rinses and the artificial saliva for 3 weeks. Two-way ANOVA, the Bonferroni test and the paired sample t-test were used for statistical analyses (p<0.05). Results: Comparison of the discoloration from the oral rinses after immersion for three weeks revealed no significant differences (p>0.05). The lowest color change was observed in PMMA-based Temdent in all oral rinses (p<0.05). There were no significant differences between the bis-acryl composites after immersion in saliva or the mixture of benzydamine HCl and chlorhexidine and the alcohol-containing mouthwash for 3 weeks (p>0.05). After immersion in chlorhexidine, the color change values of Protemp II and Fill-in showed significant differences (p=0.018). Protemp II also showed less discoloration than the other bis-acryl composites, and this color change was statistically significant (p <0.05). For all oral rinses, the L* value decreased while b* values increased, and this color change was found to be statistically significant (p <0.05). A* values were found to be significantly higher with oral rinses (p<0.05), except Protemp II immersed in benzydamine HCl or alcohol-containing mouthwash. Conclusions: The type of the oral rinse did not affect the discoloration process. For long-term esthetic results, choosing MMA-based materials for provisional restorations appears to be more effective.

Impact of Dental and Zygomatic Implants on Stress Distribution in Maxillary Defects: A 3-Dimensional Finite Element Analysis Study

The aim of this study was to evaluate the stress distribution in the bone around dental and zygomatic implants for 4 different implant-supported obturator prostheses designs in a unilaterally maxillary defect using a 3-dimensional finite element stress analysis. A 3-dimensional finite element model of the human unilateral maxillary defect was constructed. Four different implant-supported obturator prostheses were modeled; model 1 with 2 zygomatic implants and 1 dental implant, model 2 with 2 zygomatic implants and 2 dental implants, model 3 with 2 zygomatic implants and 3 dental implants, and model 4 with 1 zygomatic implant and 3 dental implants. Bar attachments were used as superstructure. A 150-N vertical load was applied in 3 different ways, and von Mises stresses in the cortical bone around implants were evaluated. When the models (model 1-3) were compared in terms of number of implants, all of the models showed similar highest stress values under the first loading condition, and these values were less than under model 4 conditions. The highest stress values of models 1-4 under the first loading condition were 8.56, 8.59, 8.32, and 11.55 Mpa, respectively. The same trend was also observed under the other loading conditions. It may be concluded that the use of a zygomatic implant on the nondefective side decreased the highest stress values, and increasing the number of dental implants between the most distal and most mesial implants on the nondefective side did not decrease the highest stress values.

Rehabilitation of an extracted anterior tooth space using fiber‐reinforced composite and the natural tooth

Conservative solutions for the restoration of a single edentulous space in the anterior maxilla present an esthetic challenge to the clinician. A 45-year-old male patient whose right upper central tooth was planned to be extracted was referred to our clinic for a conservative, rapid, and economic treatment. After radiographic and clinical examinations, it was decided that the tooth which was to be extracted should be used for the restoration of its own extracted area. The extracted tooth was splinted to adjacent teeth with the aid of the grooves and fiber-reinforced composite (everStick, StickTech Ltd., Turku, Finland). Following an early and unexpected failure of the restoration, the fiber layer was thickened twice with a flowable composite resin (Stick Flow, Stick Tech Ltd.) which fit better to the grooves. The restoration satisfied the patient with a good mechanical behavior, esthetics, and long-term durability after 12 months while. Restoring the missing tooth area with the patients own tooth is advantageous when combined with modern adhesive techniques. The clinician must pay attention to the mechanical adaptation of the restoration and the technique sensitivity of the applied adhesive system.

How will surface treatments affect the translucency of porcelain laminate veneers

PURPOSE The purpose of this study was to evaluate whether surface treatments affect the translucency of laminate veneers with different shades and thicknesses. MATERIALS AND METHODS A total of 224 disc-shaped ceramic veneers were prepared from A1, A3, HT (High Translucent) and HO (High Opaque) shades of IPS e.max Press (Ivoclar Vivadent) with 0.5 mm and 1.0 mm thicknesses. The ceramics were divided into four groups for surface treatments. Group C: no surface treatments; Group HF: etched with hydrofluoric acid; Group SB: sandblasted with 50-µm Al2O3; and Group L; irradiated with an Er;YAG laser. A translucent shade of resin cement (Rely X Veneer, 3M ESPE) was chosen for cementation. The color values of the veneers were measured with a colorimeter and translucency parameter (TP) values were calculated. A three-way ANOVA with interactions for TP values was performed and Bonferroni tests were used when appropriate (α=0.05). RESULTS There were significant interactions between the surface treatments, ceramic shades and thicknesses (P=.001). For the 0.5-mm-thick specimens there were significant differences after the SB and L treatments. There was no significant difference between the HF and C treatments for any shades or thicknesses (P>.05). For the 1-mm-thick ceramics, there was only a significant difference between the L and C treatments for the HT shade ceramics (P=.01). There were also significant differences between the SB and C treatments except not for the HO shades (P=.768). CONCLUSION The SB and L treatments caused laminate veneers to become more opaque; however, HF treatment did not affect the TP values. When the laminate veneers were thinner, both the shade of the ceramic and the SB and laser treatments had a greater effect on the TP values.

Do surface treatments affect the optical properties of ceramic veneers

STATEMENT OF PROBLEM Surface treatments may affect the optical properties of ceramic veneers before cementation. PURPOSE The purpose of this study was to evaluate whether various surface treatments affect the optical properties of different types of ceramic veneers. MATERIAL AND METHODS Disk-shaped ceramic veneers (N=280) were prepared from the IPS e.max Press, e.max CAD, Empress Esthetic, e.max Ceram, and Inline ceramic systems with 0.5-mm and 1.0-mm thicknesses. The ceramics were divided into 4 groups: no surface treatments; etched with hydrofluoric acid; airborne-particle abraded with 30-μm Al2O3; and irradiated with erbium:yttrium-aluminum-garnet laser. A translucent shade of resin was chosen for cementation. Color parameters were examined with a colorimeter. Statistical analyses were done with 3-way ANOVA and the Bonferroni test (P=.05). RESULTS Significant interactions were noted between the surface treatments, ceramic type, and thickness for ΔE values (P=.01), and no significant interactions were noted for L* (P=.773), a* (P=.984), and b* (P=.998). The greatest color change occurred after airborne-particle abrasion with 0.5-mm-thick e.max Press (2.9 ΔE). Significant differences in ΔE values were found among the hydrofluoric acid, airborne-particle abrasion, and laser groups for 0.5-mm-thick ceramics, except IPS Inline, and among the hydrofluoric acid, airborne-particle abrasion, and laser groups for 1.0-mm-thick ceramics, except Empress Esthetic ceramics. CONCLUSIONS The color change of the ceramics increased after the surface treatments, particularly as the ceramics became thinner.

Peel strength of denture liner to PMMA and polyamide: laser versus air-abrasion

PURPOSE This study investigated the effect of laser parameters and air-abrasion on the peel strength of silicon-based soft denture liner to different denture resins. MATERIALS AND METHODS Specimens (N=180) were prepared out of three different denture base resins (Rodex, cross-linked denture base acrylic resin; Paladent, heat-cured acrylic resin; Deflex, Polyamide resin) (75 mm × 25 mm × 3 mm). A silicon-based soft denture liner (Molloplast B) was applied to the denture resins after the following conditioning methods: a) Air-abrasion (50 µm), b) Er,Cr:YSGG laser (Waterlase MD Turbo, Biolase Technology) at 2 W-20 Hz, c) Er,Cr:YSGG laser at 2 W-30 Hz, d) Er,Cr:YSGG laser at 3 W-20 Hz, e) Er,Cr:YSGG laser at 3 W-30 Hz. Non-conditioned group acted as the control group. Peel test was performed in a universal testing machine. Failure modes were evaluated visually. Data were analyzed using two-way ANOVA and Tukeys test (α=.05). RESULTS Denture liner tested showed increased peel strength after laser treatment with different parameters (3.9±0.4 - 5.58±0.6 MPa) compared to the control (3.64±0.5 - 4.58±0.5 MPa) and air-abraded groups (3.1±0.6 - 4.46±0.3 MPa), but the results were not statistically significant except for Paladent, with the pretreatment of Er,Cr:YSGG laser at 3 W-20 Hz. Polyamide resin after air-abrasion showed significantly lower peel strength than those of other groups (3.1±0.6 MPa). CONCLUSION Heat-cured acrylic resin, PMMA, may benefit from Er,Cr:YSGG laser treatment at 3 W-20 Hz irradiation. Air-abrasion of polyamide resins should be avoided not to impair their peel bond strengths to silicon-based soft denture liners.

Peri-Implant Plastic Surgical Approaches to Increasing Keratinized Mucosa Width: Which to Use and When?

The long-term efficacy of adequate keratinized mucosa (>2 mm) in dental implants is controversial. Peri-implant plastic surgeries are currently used because they increase keratinized mucosa width (KMW), helping to regain peri-implant health and maintaining it over the long-term. We present the clinical findings using free-gingival-graft (FGG) and free-periosteal-graft (FPG) techniques in peri-implant plastic surgery for implant rehabilitation patients. We included 20 patients with implant indications of inadequate KMW (KMW < 2 mm for postimplantation) in the maxilla and mandible. All underwent clinical and radiographic measurements and a treatment protocol was prepared for implant rehabilitation and subsequent peri-implant plastic surgery. A decision as to whether and when FGG or FPG techniques would be used was made. FGG/FPG was performed pre-implantation (before monocortical block-bone augmentation) or postimplantation (before/during/after stage 2 surgery). KMW was ≥ 2 mm after application of FGG/FPG pre- or post-implantation. Moreover, peri-implant tissue health was regained/maintained in all cases from 6 months to 4 years. Peri-implant plastic surgery techniques can prevent hard- and soft-tissue problems after implant rehabilitation and during treatment of developing problems. However, surgical design and timing, and an interdisciplinary perspective determine the success of peri-implant plastic surgery.

Effects of Protective Resin Coating on the Surface Roughness and Color Stability of Resin-Based Restorative Materials

The aim of this study was to evaluate the effects of nanofilled protective resin coating (RC) on the surface roughness (Ra) and color stability (ΔE) of resin-based restorative materials (RM) (compomer (C), nanofilled composite (NF), and microhybrid composite (MH)) after being submitted to the ultraviolet aging (UV) method. Thirty-six specimens were prepared (n = 6 for each group). The Ra and (ΔE) values and SEM images were obtained before and after UV. Significant interactions were found among the RM-RC-UV procedures for Ra (P < 0.001). After the specimens were submitted to UV, the Ra values were significantly increased, regardless of the RC procedure (with RC; P < 0.01 for all, without RC; C (P < 0.01), NF (P < 0.001), and MH (P < 0.001)) for each RM. Significant interactions were found between the RM-RC (P < 0.001) procedures for the ΔE values. The ΔE values were increased in each group after applying the RC procedures (P < 0.001). Protective RC usage for RM could result in material-related differences in Ra and ΔE as with used UV method.

The effect of an erbium, chromium: yttrium-scandium-gallium-garnet laser on the microleakage and bond strength of silorane and micro-hybrid composite restorations

Objective: The aim of this in vitro study was to compare the microleakage and bond strength of Class V silorane-based and universal micro-hybrid composite restorations prepared either with diamond bur or with an erbium, chromium: yttrium-scandium-gallium-garnet (Er, Cr:YSGG) laser. Materials and Methods: A total of 160 molar teeth were used for microleakage assessment and shear bond strength (SBS) test. The specimens were prepared using either diamond bur or 3 W-, 4 W- and 5 W-20 Hz Er, Cr:YSGG laser irradiation. All specimens were subjected to thermocycling (500 times at 5 ± 2°C to 55 ± 2°C, dwell time 15 s and transfer time 10 s). Microleakage was assessed using a 0.5% basic-fuchsin solution. The bond strengths were determined using a microtensile tester at a crosshead speed of 0.5 mm/min. The Kruskal Wallis test was used for the analysis of microleakage and a one-way analysis of variance test was used to analyze the SBS (P < 0.05). Results: No statistically significant differences were found (P > 0.05) between Er, Cr:YSGG laser and bur preparation methods regarding microleakage and bond strength values. Conclusion: Irradiation with Er, Cr:YSGG laser was confirmed to be as effective as conventional methods for preparing cavities before adhesive restorations.