Characterization of Sn–Co Nanowires Grown into Alumina Template

Nanowires of Sn-Co alloys were grown inside the channels of anodic alumina membrane by potentiostatic deposition. The scanning electron microscope images showed the formation of cylindrical nanowires whose height was increasing with deposition time. The X-ray patterns did not show significant diffraction peaks, suggesting the formation of amorphous phases. The higher content of Co in the nanowires, in comparison to the initial composition of the electrolytic bath, was attributed to a higher rate of Co electrodeposition. These nanowires seem to possess specific features suitable for innovative application in the field of Li-ion batteries due to their dimensional stability and high specific surface.

Nanostructured Anode Material for Li-Ion Batteries

The present paper focuses on a nanostructured SnCo alloy electrochemically prepared by template method in view of its use as anode material alternative to graphite in lithium-ion batteries. The fabrication of SnCo nanowire arrays was carried out by potentiostatic co-deposition of the two metals by using nanostructured anodic alumina membranes as template. Electrochemical tests on lithiation-delithiation of these SnCo electrodes in conventional organic electrolyte (EC:DMC LiPF6) at 30°C showed that their specific capacity was stable for about the first 12 cycles at a value near to the theoretical one for Li22Sn5 and, hence, progressively decayed.