H.A.A. Sidek

Preparation and elastic moduli of germanate glass containing lead and bismuth.

This paper reports the rapid melt quenching technique preparation for the new family of bismuth-lead germanate glass (BPG) systems in the form of (GeO2)60–(PbO)40−x–(½Bi2O3)x where x = 0 to 40 mol%. Their densities with respect of Bi2O3 concentration were determined using Archimedes’ method with acetone as a floatation medium. The current experimental data are compared with those of bismuth lead borate (B2O3)20–(PbO)80−x–(Bi2O3)x. The elastic properties of BPG were studied using the ultrasonic pulse-echo technique where both longitudinal and transverse sound wave velocities have been measured in each glass samples at a frequency of 15 MHz and at room temperature. Experimental data shows that all the physical parameters of BPG including density and molar volume, both longitudinal and transverse velocities increase linearly with increasing of Bi2O3 content in the germanate glass network. Their elastic moduli such as longitudinal, shear and Young’s also increase linearly with addition of Bi2O3 but the bulk modulus did not. The Poisson’s ratio and fractal dimensionality are also found to vary linearly with the Bi2O3 concentration.

Infrared Study of Er3+/Yb3+ Co-Doped GeO2-PbO-Bi2O3 Glass

Heavy metal oxide glasses, containing bismuth and/or lead in their glass structure are new alternatives for rare eart (RE) doped hosts. Hence, the study of the structure of these vitreous systems is of great interest for science and technology. In this research work, GeO2-PbO-Bi2O3 glass host doped with Er3+/Yb3+ ions was synthesized by a conventional melt quenching method. The Fourier transform infrared (FTIR) results showed that PbO and Bi2O3 participate with PbO4 tetragonal pyramids and strongly distort BiO6 octahedral units in the glass network, which subsequently act as modifiers in glass structure. These results also confirmed the existence of both four and six coordination of germanium oxide in glass matrix.

Effects of Calcination Holding Time on Properties of Wide Band Gap Willemite Semiconductor Nanoparticles by the Polymer Thermal Treatment Method

Willemite is a wide band gap semiconductor used in modern day technology for optoelectronics application. In this study, a new simple technique with less energy consumption is proposed. Willemite nanoparticles (NPs) were produced via a water–based solution consisting of a metallic precursor, polyvinylpyrrolidone (PVP), and underwent a calcination process at 900 °C for several holding times between 1–4 h. The FT–IR and Raman spectra indicated the presence of metal oxide bands as well as the effective removal of PVP. The degree of the crystallization and formation of the NPs were determined by XRD. The mean crystallite size of the NPs was between 18.23–27.40 nm. The morphology, particle shape and size distribution were viewed with HR-TEM and FESEM analysis. The willemite NPs aggregate from the smaller to larger particles with an increase in calcination holding time from 1–4 h with the sizes ranging between 19.74–29.71 nm. The energy values obtained from the experimental band gap decreased with increasing the holding time over the range of 5.39 eV at 1 h to at 5.27 at 4 h. These values match well with band gap obtained from the Mott and Davis model for direct transition. The findings in this study are very promising and can justify the use of these novel materials as a potential candidate for green luminescent optoelectronic applications.

Elastic Constants of (TeO2)90(AlF3)10−x(ZnO)x Zinc Oxyfluorotellurite Glasses

New series of ternary tellurite glasses in the form (TeO2)90(A1F3)90−x(ZnO)x have been successfully synthesized. Both longitudinal and shear ultrasonic velocities were measured in different compositions of the glass system by using the MBS8000 Ultrasonic Data Acquisition System at 10 MHz frequency and at room temperature. The elastic properties of ternary telluirte glasses (TeO2)90(A1F3)90−x(ZnO)x were measured as a function of composition. The ultrasonic velocity data, the density, the calculated elastic moduli and micro-hardness are composition dependent and discussed in terms of ZnO modifiers that were expected to change the physical properties of oxyfluotellurite glasses.